Re-Austenitisation of Thin Ferrite Films in C–Mn Steels during Thermal Rebound at Continuously Cast Slab Corner Surfaces
The influence of primary cooling and rebound temperature at C–Mn slab corner surfaces during continuous casting on ferrite film transformation and AlN precipitation was investigated. Laboratory simulations included primary cooling to minimum temperature, <i>T<sub>min</sub></i>...
Main Authors: | Dannis Rorisang Nkarapa Maubane, Roelf Johannes Mostert, Kevin Mark Banks |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-12-01
|
Series: | Metals |
Subjects: | |
Online Access: | https://www.mdpi.com/2075-4701/12/12/2155 |
Similar Items
-
Beta-blocker Rebound Phenomenon in an Adolescent with Graves’ Disease
by: Ahmet Anık
Published: (2022-12-01) -
Timing of Adiposity Rebound and Determinants of Early Adiposity Rebound in Korean Infants and Children Based on Data from the National Health Insurance Service
by: Eun Kyoung Goh, et al.
Published: (2022-02-01) -
Effect of Nitriding Process on Wear Behavior of Dual Phase (Ferrite+Martensite) Ductile Cast Iron
by: Elif ERDOĞAN, et al.
Published: (2022-03-01) -
Research on the rebound rule of a pit bottom caused by excavation of typical strata
by: Qingyuan Yang, et al.
Published: (2024-04-01) -
Effects of ferrite and graphite phases on scratch characteristics of nodular cast iron
by: Zhitong Xu, et al.
Published: (2024-05-01)