Microstructural Evolution of Large Cast Haynes 282 at Elevated Temperature

Microstructural Evolution of Large Cast Haynes 282 at Elevated Temperature

Haynes 282 has attracted attention for casting applications in AUSC power plants due to its good creep properties. However, the market is primarily comprised of wrought Haynes 282, while the cast version is not commercially available. In this study, the microstructure of a large traditional sand cas...

Mô tả đầy đủ

Chi tiết về thư mục
Tác giả chính:	Yujin Yang
Định dạng:	Bài viết
Ngôn ngữ:	English
Được phát hành:	MDPI AG 2021-07-01
Loạt:	Crystals
Những chủ đề:	Haynes 282 large sand cast microstructural evolution
Truy cập trực tuyến:	https://www.mdpi.com/2073-4352/11/8/867

Những quyển sách tương tự

Optimization of large cast Haynes 282 based on thermal induced cracks: formation and elimination
Bằng: Yang Yujin
Được phát hành: (2024-01-01)

Finishing Turning of Ni Superalloy Haynes 282
Bằng: José Díaz-Álvarez, et al.
Được phát hành: (2018-10-01)

Sustainable High-Speed Finishing Turning of Haynes 282 Using Carbide Tools in Dry Conditions
Bằng: Antonio Díaz-Álvarez, et al.
Được phát hành: (2019-09-01)

High-Pressure Cooling in Finishing Turning of Haynes 282 Using Carbide Tools: Haynes 282 and Inconel 718 Comparison
Bằng: Antonio Díaz-Álvarez, et al.
Được phát hành: (2021-11-01)

Heat-Affected-Zone Liquation Cracking in Welded Cast Haynes<sup>®</sup> 282<sup>®</sup>
Bằng: Sukhdeep Singh, et al.
Được phát hành: (2019-12-01)

Microstructure and mechanical properties of dissimilar diffusion bonded joints of Haynes 230 and Haynes 188 superalloys
Bằng: Zhaoxi Li, et al.
Được phát hành: (2024-03-01)

Thermo-Viscoplastic Behavior of Ni-Based Superalloy Haynes 282 and Its Application to Machining Simulation
Bằng: Marcos Rodríguez-Millán, et al.
Được phát hành: (2017-12-01)

Roadmap for additive manufacturing of HAYNES® 282® superalloy by laser beam powder bed fusion (PBF-LB) technology
Bằng: Robert Otto, et al.
Được phát hành: (2021-06-01)

Friction stir welding of Haynes 282 Ni superalloy by using a novel hemispherical tool
Bằng: Abhishek Sharma, et al.
Được phát hành: (2024-11-01)

On the effect of building platform material on laser-powder bed fusion of a Ni-base superalloy HAYNES® 282®
Bằng: Abdul Shaafi Shaikh, et al.
Được phát hành: (2022-10-01)

Effect of Post Processing Heat Treatment Routes on Microstructure and Mechanical Property Evolution of Haynes 282 Ni-Based Superalloy Fabricated with Selective Laser Melting (SLM)
Bằng: Anagh Deshpande, et al.
Được phát hành: (2020-05-01)

High-Temperature Creep and Microstructure Evolution of Alloy 800H Weldments with Inconel 625 and Haynes 230 Filler Materials
Bằng: Wenjing Li, et al.
Được phát hành: (2024-02-01)

Microstructure evolution and work hardening behaviour during cold deformation of Haynes 214 superalloy
Bằng: Jiaao Liu, et al.
Được phát hành: (2023-05-01)

Temperature dependent tensile behavior of additively manufactured HAYNES® 214: A comparative study between laser powder bed fusion and laser powder directed energy deposition
Bằng: Shaharyar Baig, et al.
Được phát hành: (2024-09-01)

Haynes 242 Alloy for LARES 2 Satellite
Bằng: D. Pilone, et al.
Được phát hành: (2021-04-01)

SPACE AS A MEANS OF (NON)COMMUNICATION IN MICHELANGELO ANTONIONI’S RED DESERT AND TODD HAYNES’ SAFE
Bằng: Dejan M. Malčić
Được phát hành: (2022-06-01)

Towards the reform of medieval mendicant orders. Exhortatio ad meditationem et conformationem passionis Christi by Maciej Hayn (†1477)
Bằng: Adam Poznański
Được phát hành: (2012-12-01)

Significantly improved weldability in laser welding of additively manufactured haynes 230 superalloys by tailoring microstructure
Bằng: Danyang lin, et al.
Được phát hành: (2023-09-01)

Effect of boron addition on the microstructure and mechanical property of cobalt-based haynes 188 alloy
Bằng: Dan Jia, et al.
Được phát hành: (2025-03-01)

Effect of Alloying Additives and Casting Parameters on the Microstructure and Mechanical Properties of Silicon Bronzes
Bằng: D. Witasiak, et al.
Được phát hành: (2023-09-01)

Kate Winslet dans Mildred Pierce de Todd Haynes (HBO, 2011) : enjeux d’un passage du grand au petit écran
Bằng: Céline Bintein
Được phát hành: (2022-04-01)

Comparative Study on Microstructure and Corrosion Resistance of Al-Si Alloy Cast from Sand Mold and Binder Jetting Mold
Bằng: María Ángeles Castro-Sastre, et al.
Được phát hành: (2021-09-01)

Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy
Bằng: Lixiang Yang, et al.
Được phát hành: (2023-08-01)

بررسی اثر کار گرم و آنیل انحلالی بر ریزساختار و خواص مکانیکی سوپرآلیاژ Haynes 188
Bằng: مهدی سمیعی زفرقندی, et al.
Được phát hành: (2020-02-01)

Microstructure Evolution During the Sintering of Freeze-Cast Alumina
Bằng: Daniel D. Athayde, et al.
Được phát hành: (2024-02-01)

A customised novel hybrid post-treatment process achieved excellent mechanical properties in additively manufactured Haynes 230 alloy
Bằng: Wenjie Liu, et al.
Được phát hành: (2024-12-01)

The sand casting process modeling [electronic resource] /
Bằng: Mohd. Fairus Yahaya, 1985-, et al.
Được phát hành: (2008)

Typical microstructures of cast metals /
Bằng: Boultbee, E. F., et al.
Được phát hành: (1981)

Effect of casting temperature on the microstructure of as-cast GH625 alloy
Bằng: WANG Hao-yu, et al.
Được phát hành: (2015-11-01)

Evolution of microstructure in centrifugal cast Al-Cu alloy
Bằng: Sui Yanwei, et al.
Được phát hành: (2010-02-01)

Multi-scale crack closure measurements with digital image correlation on Haynes 230
Bằng: Stefano Beretta, et al.
Được phát hành: (2015-07-01)

Microstructural characterisation related to hot tearing of Al-Cu sand mould castings
Bằng: Mattia Merlin
Được phát hành: (2010-10-01)

Effect of Solidification Rates at Sand Casting on the Mechanical Joinability of a Cast Aluminium Alloy
Bằng: Moritz Neuser, et al.
Được phát hành: (2021-08-01)

Effect of heat treatment on the microstructures and mechanical properties of the sand-cast Mg–2.7Nd–0.6Zn–0.5Zr alloy
Bằng: D. Wu, et al.
Được phát hành: (2014-03-01)

Microstructural Evolution as a Function of Increasing Aluminum Content in Novel Lightweight Cast Irons
Bằng: Alejandro Obregon, et al.
Được phát hành: (2021-10-01)

Simulation of sand casting of automotive part using anycasting and DOE method /
Bằng: Shedee Bahari, 1988-, et al.
Được phát hành: (2011)

Microstructure of Reinforced Cast Iron Produced by Lost Foam Casting
Bằng: Pavlo Kaliuzhnyi, et al.
Được phát hành: (2023-12-01)

Casting Defects in Sand-Mold Cast Irons—An Illustrated Review with Emphasis on Spheroidal Graphite Cast Irons
Bằng: Jon Sertucha, et al.
Được phát hành: (2022-03-01)

Barley Malt as a Binder for Moulding Sands—Gas Evolution and Surface Quality of Iron Castings
Bằng: Daniel Nowak, et al.
Được phát hành: (2024-04-01)

Simulation of sand casting of automotive part using anycasting and DOE method [electronic resource] /
Bằng: Shedee Bahari, 1988-, et al.
Được phát hành: (2011)