Correlation Between Eutectoid Phase Transition and Deuteration Kinetics of TiHf Alloys
Using a method of constant volume and alterable pressure, deuteration kinetics of TiHfx(x=0.13, 0.26, 0.52) alloys and Hf were studied at the same initial pressures and in the temperature range of 473 to 873 K. The correlation of decrease of deuterium pressure with time was attained by the experime...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Board of Journal of Isotopes
2014-02-01
|
| Series: | Journal of Isotopes |
| Subjects: | |
| Online Access: | http://www.tws.org.cn/CN/10.7538/tws.2014.27.01.0041 |
| Summary: | Using a method of constant volume and alterable pressure, deuteration kinetics of TiHfx(x=0.13, 0.26, 0.52) alloys and Hf were studied at the same initial pressures and in the temperature range of 473 to 873 K. The correlation of decrease of deuterium pressure with time was attained by the experiment of alloys absorbing deuterium. According to the results，the main factors that decide kinetics of Ti-Hf alloys absorbing deuterium were put forward and discussed. In the temperature range of 473 to 873 K, the deuteration curves of Ti-Hf alloys present two distinct figure in the higher or lower temperature region, which implies dissimilar reaction mechanism. Above 673 K, the α→β phase transition take place when Ti-Hf alloys react with deuterium gas. But that will be a α→δ phase transition as the temperature below 673 K. Thereby, it will be confirmed that the eutectoid phase transition temperature of TiHfx-D system is about 673 K. With x of TiHfx bigger, the eutectoid phase transition temperature become higher. |
|---|---|
| ISSN: | 1000-7512 1000-7512 |