Creep-fatigue life evaluation of circular notch specimen on a CrMoV forging steel under multiaxial stress gradient condition
Creep-fatigue damage preferentially exceeds at stress concentration portions in high temperature components such as steam turbine rotors during cyclic start up- shut down operation. Therefore development of an accurate crack initiation life assessment method under creep-fatigue conditions at the str...