| Summary: | Carbon black-reinforced rubber compounds based on the blends of natural rubber (NR) and butadiene rubber (BR) for tire sidewall applications were formulated to investigate the self-healing efficacy of a modifier called EMZ. This modifier is based on epoxidized natural rubber (ENR) modified with hydrolyzed maleic anhydride (HMA) as the ester crosslinking agent plus zinc acetate dihydrate (ZAD) as the transesterification catalyst. The influence of EMZ modifier content in sidewall compounds on processing characteristics, reinforcement, mechanical and fatigue properties, as well as property retentions, was investigated. Increasing the content of EMZ, the dump temperatures and Mooney viscosities of the compounds slightly increase, attributed to the presence of extra polymer networks and filler–rubber interactions. The bound rubber content and Payne effect show a good correction that essentially supports that the EMZ modifier gives enhanced filler–rubber interaction and reduced filler–filler interaction, reflecting the improved homogeneity of the composites. This is the key contribution to a better flex cracking resistance and a high fatigue-to-failure resistance when utilizing the EMZ modifier. To validate the property retentions, molecular damages were introduced to vulcanizates using a tensile stress–strain cyclic test following the Mullins effect concept. The property retentions are significantly enhanced with increasing EMZ content because the EMZ self-healing modifier provides reversible or dynamic ester linkages that potentially enable a bond-interchange mechanism of the crosslinks, leading to the intermolecular reparation of the rubber network.
|
|---|