| Summary: | Carbonated hydroxyapatite (CHA) microspheres have aroused wide concern in biofields because of their excellent biological and surface properties. However, the facile preparation of CHA microspheres from organic compounds, especially the microstructural transformation during synthesis, has been rarely reported. In this work, CHA microspheres with an average diameter of 2.528 μm and a BET surface area of 51.0658 m<sup>2</sup>/g were synthesized via a one-pot hydrothermal method at 180 °C for 10 h by using calcium chloride, diammonium hydrogen phosphate, urea, and trisodium citrate (TSC) with a molar ratio of TSC to Ca of 1:2. The effects of hydrothermal treatment temperature and molar ratio of TSC to Ca on the morphology of the products were investigated. As a chelating agent, TSC is crucial to the formation of CHA microspheres during the hydrothermal homogeneous precipitation process. A possible mechanism of the microstructural transformation from bundle to dumbbell, dumbbell ball, and finally, microspheres regulated by TSC and urea was proposed. The CHA microspheres can be used as effective drug carriers for biomedical applications.
|
|---|