Preparation of Magnesia Partially Stabilized Zirconia Nanomaterials from Zirconium Hydroxide and Magnesium Carbonate Precursors Using PEG as a Template
Stabilized zirconia is a promising material due to its great physical and chemical properties, and thermal stability. In this work, MgO was used as a stabilizer in ZrO<sub>2</sub> to obtain Magnesia Partially Stabilized Zirconia (MSZ) nanomaterials assisted with PEG as a template through...
Main Authors: | Rizky Berliana Wijayanti, Irna Rosmayanti, Kristanto Wahyudi, Eneng Maryani, Hernawan Hernawan, Rifki Septawendar |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2021-06-01
|
Series: | Crystals |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4352/11/6/635 |
Similar Items
-
Low-calcination temperatures of magnesia partially stabilized zirconia (Mg-PSZ) nanoparticles derived from local zirconium silicates
by: Kristanto Wahyudi, et al.
Published: (2021-01-01) -
Zirconium Oxide and Iron Zirconate Obtained from Citrus Pectin and Nitrates Applied in the Photo-fenton-like Process
by: Cristiane Antoniazzi, et al.
Published: (2018-06-01) -
Russian zirconium industry: current issues in raw material supply
by: Vitaly Yu. Khatkov, et al.
Published: (2023-06-01) -
The Effect of Sulfated Zirconia and Zirconium Phosphate Nanocomposite Membranes on Fuel-Cell Efficiency
by: Rudzani Sigwadi, et al.
Published: (2022-01-01) -
Zirconium /
by: 376428 Miller, George Leslie
Published: (1954)