Creep and Oxidation Behaviors of 25 wt.% Cr–Containing Nickel-Based Alloys Reinforced by ZrC Carbides
Three alloys based on nickel, rich in chromium due to their oxidation resistance at high temperature and containing ZrC carbides for their mechanical reinforcing against creep, were elaborated by foundry. After control of their as-cast microstructures, these alloys were subjected at 1100 °C to flexu...
Main Authors: | Patrice Berthod, Safa Tlili |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2022-03-01
|
Series: | Crystals |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4352/12/3/416 |
Similar Items
-
Oxidation and Microstructural Behaviors at 1200 °C of 32.5 wt.% Cr–Containing Co–Based Alloys Strengthened by HfC Carbides
by: Patrice Berthod
Published: (2022-03-01) -
Oxidation and Microstructural Behaviors of Ni-Based Alloys Strengthened by (Ta, Hf)C Carbides at 1250 °C in Air
by: Patrice Berthod, et al.
Published: (2021-02-01) -
Pressureless sintering of ZrC with variable stoichiometry
by: Katrin Schönfeld, et al.
Published: (2017-06-01) -
Changes in Abrasion Resistance of Cast Cr-Ni Steel as a Result of the Formation of Niobium Carbides in Alloy Matrix
by: Grzegorz Tęcza
Published: (2023-02-01) -
Influence of the Chromium Content on the Characteristics of the Matrix, the Tantalum Carbides Population, and the Hardness of Cast Co(Cr)-0.4C-6Ta Alloys
by: Patrice Berthod, et al.
Published: (2023-02-01)