Bioactive Carbonate Apatite Cement with Enhanced Compressive Strength via Incorporation of Silica Calcium Phosphate Composites and Calcium Hydroxide
Carbonate apatite (CO<sub>3</sub>Ap) is a bioceramic material with excellent properties for bone and dentin regeneration. To enhance its mechanical strength and bioactivity, silica calcium phosphate composites (Si-CaP) and calcium hydroxide (Ca(OH)<sub>2</sub>) were added to...
Main Authors: | Arief Cahyanto, Michella Liemidia, Elin Karlina, Myrna Nurlatifah Zakaria, Khairul Anuar Shariff, Cortino Sukotjo, Ahmed El-Ghannam |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2023-03-01
|
Series: | Materials |
Subjects: | |
Online Access: | https://www.mdpi.com/1996-1944/16/5/2071 |
Similar Items
-
Calcium release and physical properties of modified carbonate apatite cement as pulp capping agent in dental application
by: Myrna Nurlatifah Zakaria, et al.
Published: (2018-12-01) -
Formation of biomimetic apatite on calcium phosphate foam ceramics in standard and carbonate-free model solutions
by: V.K. Krut’ko, et al.
Published: (2023-12-01) -
Phase composition and biocompatibility of calcium phosphate coatings on titanium enriched with hydroxyapatite
by: A.E. Doroshenko, et al.
Published: (2023-12-01) -
Carbonation inhibitor by polyethylene glycol encapsulation of calcium hydroxide fine particles to improve antimicrobial and root canal penetration properties
by: Atia Nurul Sidiqa, et al.
Published: (2023-07-01) -
Bone Tissue Regeneration by Collagen Scaffolds with Different Calcium Phosphate Coatings: Amorphous Calcium Phosphate and Low-Crystalline Apatite
by: Syama Santhakumar, et al.
Published: (2021-10-01)