Optical Properties and Growth Mechanism of La3Ga5.5Nb0.5O14 Macroporous Ceramic
Abstract Optical properties and growth mechanism of La3Ga5.5Nb0.5O14 oxides by a Pechini process were investigated. The structure and morphology were obtained after sintering at 600–800 °C. This crystallized orthorhombic La3Ga5.5Nb0.5O14 can be obtained by the heat treatment process at 800 °C from X...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
SpringerOpen
2019-08-01
|
| Series: | Nanoscale Research Letters |
| Subjects: | |
| Online Access: | http://link.springer.com/article/10.1186/s11671-019-3104-x |
| Summary: | Abstract Optical properties and growth mechanism of La3Ga5.5Nb0.5O14 oxides by a Pechini process were investigated. The structure and morphology were obtained after sintering at 600–800 °C. This crystallized orthorhombic La3Ga5.5Nb0.5O14 can be obtained by the heat treatment process at 800 °C from XRD. A proposed schematic growth mechanism of La3Ga5.5Nb0.5O14 macroporous based on the details provided is shown. The photo-luminescence spectra shown that under 327 nm excitation spectra, a broad and blue emission peak is observed at 475 nm at 77 K and this spectrum is originated from the [NbO6]7− octahedra group. The optical absorption spectra of the 800 °C sample exhibited a well-crystalline and very low oxygen vacancy, which corresponded to the band gap energies of 3.95 eV. |
|---|---|
| ISSN: | 1931-7573 1556-276X |