Evaporated Alkali Carbonate Effect on an Aluminum Diffusion Coated 253MA Vessel after 4000 h Discontinuous Operation—Lessons Learned

Evaporated Alkali Carbonate Effect on an Aluminum Diffusion Coated 253MA Vessel after 4000 h Discontinuous Operation—Lessons Learned

A vessel of a laboratory setup for hosting molten alkali carbonate immersion experiments was recently decommissioned after about 4000 h discontinuous operation at 800 °C. In this article, we want to describe the long-term damage of the vessel caused by evaporated alkali carbonate species in a carbon...

Volledige beschrijving

Bibliografische gegevens
Hoofdauteurs: Esraa Hamdy, Angelina Wagné, Christine Geers
Formaat: Artikel
Taal:English
Gepubliceerd in: MDPI AG 2022-04-01
Reeks:Energies
Onderwerpen:
high temperature corrosion
molten carbonates
alloy 253MA
aluminum powder pack diffusion coating
environmentally induced precipitation
Online toegang:https://www.mdpi.com/1996-1073/15/9/3241

Internet

https://www.mdpi.com/1996-1073/15/9/3241

Gelijkaardige items