EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHOD
SiC-B₄C composite powders were synthesised by the carbothermal reduction method under argon atmosphere by using boric acid, silica sol, and flake graphite as the raw materials. The effects of the boric acid dosage and reaction temperature on the phase composition and microstructure of the synthesise...
Main Authors: | , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
University of Chemistry and Technology, Prague
2022-04-01
|
Series: | Ceramics-Silikáty |
Subjects: | |
Online Access: |
http://www.ceramics-silikaty.cz/index.php?page=cs_detail_doi&id=1569
|
_version_ | 1797674871996547072 |
---|---|
author | Jinxiu He Jilin Hu Chen Bo Deng Ruyi Lei Dapeng |
author_facet | Jinxiu He Jilin Hu Chen Bo Deng Ruyi Lei Dapeng |
author_sort | Jinxiu He |
collection | DOAJ |
description | SiC-B₄C composite powders were synthesised by the carbothermal reduction method under argon atmosphere by using boric acid, silica sol, and flake graphite as the raw materials. The effects of the boric acid dosage and reaction temperature on the phase composition and microstructure of the synthesised SiC-B₄C composite powders were studied, and the synthesis mechanism of these powders were discussed. The results show that the suitable reaction conditions for synthesising the SiC-B₄C composite powders were kept at 1500 °C and 1550 °C for 2 h when the amounts of excess boric acid were 0 wt.%-20 wt.% and 30 wt.%, respectively. The microscopic morphology of the SiC-B₄C powder samples with a 0 wt.%-20 wt.% excess of boric acid calcined at 1500 °C for 2 h was mainly composed of flake particles, short rod-shaped particles, and a small amount of approximately spherical particles. The powder samples calcined at 1500 °C for 2 h generated not only irregular polygonal structure particles, but also a small amount of long rod-shaped particles and fibrous whiskers when the amount of excess boric acid was 30 wt.%. |
first_indexed | 2024-03-11T22:05:27Z |
format | Article |
id | doaj.art-f7cfa79a777c409db89bc42637e5c25d |
institution | Directory Open Access Journal |
issn | 0862-5468 1804-5847 |
language | English |
last_indexed | 2024-03-11T22:05:27Z |
publishDate | 2022-04-01 |
publisher | University of Chemistry and Technology, Prague |
record_format | Article |
series | Ceramics-Silikáty |
spelling | doaj.art-f7cfa79a777c409db89bc42637e5c25d2023-09-25T06:38:52ZengUniversity of Chemistry and Technology, PragueCeramics-Silikáty0862-54681804-58472022-04-0166224525410.13168/cs.2022.001910.13168/cs.2022.0019.20230925063759EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHODJinxiu He0Jilin Hu1Chen Bo2Deng Ruyi3Lei Dapeng4 Hunan Provincial Key Laboratory of Fine Ceramics and Powder Materials, School of Materials and Environmental Engineering, Hunan University of Humanities, Science and Technology, Loudi 417000, China Hunan Provincial Key Laboratory of Fine Ceramics and Powder Materials, School of Materials and Environmental Engineering, Hunan University of Humanities, Science and Technology, Loudi 417000, China Hunan Provincial Key Laboratory of Fine Ceramics and Powder Materials, School of Materials and Environmental Engineering, Hunan University of Humanities, Science and Technology, Loudi 417000, China Hunan Provincial Key Laboratory of Fine Ceramics and Powder Materials, School of Materials and Environmental Engineering, Hunan University of Humanities, Science and Technology, Loudi 417000, China Hunan Provincial Key Laboratory of Fine Ceramics and Powder Materials, School of Materials and Environmental Engineering, Hunan University of Humanities, Science and Technology, Loudi 417000, China SiC-B₄C composite powders were synthesised by the carbothermal reduction method under argon atmosphere by using boric acid, silica sol, and flake graphite as the raw materials. The effects of the boric acid dosage and reaction temperature on the phase composition and microstructure of the synthesised SiC-B₄C composite powders were studied, and the synthesis mechanism of these powders were discussed. The results show that the suitable reaction conditions for synthesising the SiC-B₄C composite powders were kept at 1500 °C and 1550 °C for 2 h when the amounts of excess boric acid were 0 wt.%-20 wt.% and 30 wt.%, respectively. The microscopic morphology of the SiC-B₄C powder samples with a 0 wt.%-20 wt.% excess of boric acid calcined at 1500 °C for 2 h was mainly composed of flake particles, short rod-shaped particles, and a small amount of approximately spherical particles. The powder samples calcined at 1500 °C for 2 h generated not only irregular polygonal structure particles, but also a small amount of long rod-shaped particles and fibrous whiskers when the amount of excess boric acid was 30 wt.%. http://www.ceramics-silikaty.cz/index.php?page=cs_detail_doi&id=1569 reaction temperature boric acid dosage carbothermal reduction method synthesis sic-b4c composite powders |
spellingShingle | Jinxiu He Jilin Hu Chen Bo Deng Ruyi Lei Dapeng EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHOD Ceramics-Silikáty reaction temperature boric acid dosage carbothermal reduction method synthesis sic-b4c composite powders |
title | EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHOD |
title_full | EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHOD |
title_fullStr | EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHOD |
title_full_unstemmed | EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHOD |
title_short | EFFECTS OF BORIC ACID DOSAGE AND REACTION TEMPERATURE ON THE PHASE COMPOSITION AND MICROSTRUCTURE OF Si C-B₄C COMPOSITE POWDERS SYNTHESISED BY THE CARBOTHERMAL REDUCTION METHOD |
title_sort | effects of boric acid dosage and reaction temperature on the phase composition and microstructure of si c b₄c composite powders synthesised by the carbothermal reduction method |
topic | reaction temperature boric acid dosage carbothermal reduction method synthesis sic-b4c composite powders |
url |
http://www.ceramics-silikaty.cz/index.php?page=cs_detail_doi&id=1569
|
work_keys_str_mv | AT jinxiuhe effectsofboricaciddosageandreactiontemperatureonthephasecompositionandmicrostructureofsicb4ccompositepowderssynthesisedbythecarbothermalreductionmethod AT jilinhu effectsofboricaciddosageandreactiontemperatureonthephasecompositionandmicrostructureofsicb4ccompositepowderssynthesisedbythecarbothermalreductionmethod AT chenbo effectsofboricaciddosageandreactiontemperatureonthephasecompositionandmicrostructureofsicb4ccompositepowderssynthesisedbythecarbothermalreductionmethod AT dengruyi effectsofboricaciddosageandreactiontemperatureonthephasecompositionandmicrostructureofsicb4ccompositepowderssynthesisedbythecarbothermalreductionmethod AT leidapeng effectsofboricaciddosageandreactiontemperatureonthephasecompositionandmicrostructureofsicb4ccompositepowderssynthesisedbythecarbothermalreductionmethod |