| Summary: | Cement production contributes significantly to carbon dioxide emissions. Alkali-activated materials offer an environmentally friendly alternative due to their comparable strength, durability and low-carbon emissions while utilizing wastes and industrial by-products. Wood ash is a waste material that shows promising results as a partial replacement for Portland cement and precursors in alkali-activated systems. The aim of this study was to examine the effect of ground wood ash on the mechanical properties of alkali-activated mortars. Wood ash was incorporated as a 0 wt%, 10 wt% and 20 wt% partial replacement for ground granulated blast furnace slag (GGBFS). The wood ashes were ground in a planetary ball mill for 10 and 20 min. Sodium silicate (Na<sub>2</sub>SiO<sub>3</sub>), sodium carbonate (Na<sub>2</sub>CO<sub>3</sub>), and sodium hydroxide (NaOH) were used as alkali activators. The results demonstrated that ground wood ash improved the mechanical properties of alkali-activated systems compared to untreated wood ash. However, the incorporation of wood ash increased the porosity of the binder matrix.
|
|---|