Different Roles of Ce<sup>3+</sup> Optical Centers in Oxyorthosilicate Nanocrystals at X-ray and UV Excitation
Luminescence properties of Lu<sub>2</sub>SiO<sub>5</sub>:Ce<sup>3+</sup> and Y<sub>2</sub>SiO<sub>5</sub>:Ce<sup>3+</sup> nanocrystals were studied using photo- and X-ray luminescence techniques. The crystal structure of Re<s...
Main Authors: | Vladyslav Seminko, Pavel Maksimchuk, Iryna Bespalova, Yuri Malyukin |
---|---|
Format: | Article |
Language: | English |
Published: |
MDPI AG
2019-02-01
|
Series: | Crystals |
Subjects: | |
Online Access: | https://www.mdpi.com/2073-4352/9/2/114 |
Similar Items
-
Thirty-Fold Increase in Relative Sensitivity of Dy<sup>3+</sup> Luminescent Boltzmann Thermometers Using Multiparameter and Multilevel Cascade Temperature Readings
by: Željka Antić, et al.
Published: (2023-05-01) -
Oscillations of Cerium Oxidation State Driven by Oxygen Diffusion in Colloidal Nanoceria (CeO2 − x )
by: Yuri Malyukin, et al.
Published: (2017-10-01) -
Ce:LiLuf4 lasers
by: Johnson, K, et al.
Published: (2003) -
INORGANIC PHOSPHORS IN GLASS BASED ON LEAD SILICATE GLASSES
by: V. A. Aseev, et al.
Published: (2014-09-01) -
YAG:Ce Nanophosphors Synthesized by the Polymer–Salt Method for White LEDs with Isomorphic Substitution of Yttrium by Gadolinium
by: Dmitry V. Bulyga, et al.
Published: (2023-07-01)