The impact of reeds residue addition on physical and mechanical properties of particleboard made from pomegranate prunings
The impact of reeds residue addition on physical and mechanical properties of particleboard made from pomegranate pruning was investigated. Laboratory particleboard was made applying one of the three levels of press time (3, 4 and 5 minutes) and one of the four levels of reed and pomegranate pru...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | fas |
| Published: |
Regional Information Center for Science and Technology (RICeST)
2012-03-01
|
| Series: | تحقیقات علوم چوب و کاغذ ایران |
| Subjects: | |
| Online Access: | http://ijwpr.areeo.ac.ir/article_117078_8f9f41335a9a1c0af826400171e28257.pdf |
| _version_ | 1828972827895660544 |
|---|---|
| author | Reza Hajihassani Hossein Hosseinkhani Abolfazl Kargarfard Fardad Golbabaei |
| author_facet | Reza Hajihassani Hossein Hosseinkhani Abolfazl Kargarfard Fardad Golbabaei |
| author_sort | Reza Hajihassani |
| collection | DOAJ |
| description | The impact of reeds residue addition on physical and mechanical properties of particleboard made from pomegranate pruning was investigated. Laboratory particleboard was made applying one of the three levels of press time (3, 4 and 5 minutes) and one of the four levels of reed and pomegranate pruning mixture (1-100% reeds; 2- 75% reeds + 25% pomegranate pruning; 3- 50% reeds + 50% pomegranate pruning and 4- 25% reeds + 75% pomegranate pruning). Boards were made in three replicate and 36 boards were made. Boards were tested using relevant EN standard and results were analyzed based on complete randomized design (CRD) under factorial experiment. Results revealed that increasing of pomegranate pruning in the wood mixture imposed positive effect on MOR, MOE, IB and thickness swelling of the particleboard. The relevant values of MOR, and MOE of the boards produced using 25% reeds + 75% pomegranate pruning were determined as 16.20 MPa and 2533 MPa respectively. Also thickness swelling after for 2 and 24 hours soaking in water decreased from 17.51 and 33.21% to 9.33 and 16.84% respectively. Internal bond strength (IB) of boards made applying 3 minutes press time (0.17 MPa.) was higher than boards made pressed for either 4 or 5 minutes, which indicates that 3 minutes press time is the appropriate time to approach maximum MOR and minimum thickness swelling after 24 hours soaking in water. |
| first_indexed | 2024-12-14T13:35:13Z |
| format | Article |
| id | doaj.art-fa764a4c256e43aaa25299be3f85e6ed |
| institution | Directory Open Access Journal |
| issn | 1735-0913 2383-112X |
| language | fas |
| last_indexed | 2024-12-14T13:35:13Z |
| publishDate | 2012-03-01 |
| publisher | Regional Information Center for Science and Technology (RICeST) |
| record_format | Article |
| series | تحقیقات علوم چوب و کاغذ ایران |
| spelling | doaj.art-fa764a4c256e43aaa25299be3f85e6ed2022-12-21T22:59:36ZfasRegional Information Center for Science and Technology (RICeST)تحقیقات علوم چوب و کاغذ ایران1735-09132383-112X2012-03-01271385010.22092/ijwpr.2012.117078117078The impact of reeds residue addition on physical and mechanical properties of particleboard made from pomegranate pruningsReza Hajihassani0Hossein Hosseinkhani1Abolfazl Kargarfard2Fardad Golbabaei3PhD, Wood and forest products division, Research Institute of Forests and Rangelands, Agricultural Research Education and Extension Organization (AREEO), Tehran, IranWood Science & Forest Products Research Division Research Institute of Forests & Rangelands Tehran, IranWood and Forest Products Science Research Division, Research Institute of Forests and Rangelands, Tehran, Iran,Wood and Forest Products Science Research Division, Research Institute of Forests and Rangelands, Agricultural Research Education and Extension Organization (AREEO) P.O. Box 13185-116, Tehran, IranThe impact of reeds residue addition on physical and mechanical properties of particleboard made from pomegranate pruning was investigated. Laboratory particleboard was made applying one of the three levels of press time (3, 4 and 5 minutes) and one of the four levels of reed and pomegranate pruning mixture (1-100% reeds; 2- 75% reeds + 25% pomegranate pruning; 3- 50% reeds + 50% pomegranate pruning and 4- 25% reeds + 75% pomegranate pruning). Boards were made in three replicate and 36 boards were made. Boards were tested using relevant EN standard and results were analyzed based on complete randomized design (CRD) under factorial experiment. Results revealed that increasing of pomegranate pruning in the wood mixture imposed positive effect on MOR, MOE, IB and thickness swelling of the particleboard. The relevant values of MOR, and MOE of the boards produced using 25% reeds + 75% pomegranate pruning were determined as 16.20 MPa and 2533 MPa respectively. Also thickness swelling after for 2 and 24 hours soaking in water decreased from 17.51 and 33.21% to 9.33 and 16.84% respectively. Internal bond strength (IB) of boards made applying 3 minutes press time (0.17 MPa.) was higher than boards made pressed for either 4 or 5 minutes, which indicates that 3 minutes press time is the appropriate time to approach maximum MOR and minimum thickness swelling after 24 hours soaking in water.http://ijwpr.areeo.ac.ir/article_117078_8f9f41335a9a1c0af826400171e28257.pdfPARTICLEBOARDREEDmodulus of rupture (MOR)MODULUS OF ELASTICITY (MOE)internal bond strength (IB)Thickness swelling |
| spellingShingle | Reza Hajihassani Hossein Hosseinkhani Abolfazl Kargarfard Fardad Golbabaei The impact of reeds residue addition on physical and mechanical properties of particleboard made from pomegranate prunings تحقیقات علوم چوب و کاغذ ایران PARTICLEBOARD REED modulus of rupture (MOR) MODULUS OF ELASTICITY (MOE) internal bond strength (IB) Thickness swelling |
| title | The impact of reeds residue addition on physical and mechanical properties
of particleboard made from pomegranate prunings |
| title_full | The impact of reeds residue addition on physical and mechanical properties
of particleboard made from pomegranate prunings |
| title_fullStr | The impact of reeds residue addition on physical and mechanical properties
of particleboard made from pomegranate prunings |
| title_full_unstemmed | The impact of reeds residue addition on physical and mechanical properties
of particleboard made from pomegranate prunings |
| title_short | The impact of reeds residue addition on physical and mechanical properties
of particleboard made from pomegranate prunings |
| title_sort | impact of reeds residue addition on physical and mechanical properties of particleboard made from pomegranate prunings |
| topic | PARTICLEBOARD REED modulus of rupture (MOR) MODULUS OF ELASTICITY (MOE) internal bond strength (IB) Thickness swelling |
| url | http://ijwpr.areeo.ac.ir/article_117078_8f9f41335a9a1c0af826400171e28257.pdf |
| work_keys_str_mv | AT rezahajihassani theimpactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings AT hosseinhosseinkhani theimpactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings AT abolfazlkargarfard theimpactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings AT fardadgolbabaei theimpactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings AT rezahajihassani impactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings AT hosseinhosseinkhani impactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings AT abolfazlkargarfard impactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings AT fardadgolbabaei impactofreedsresidueadditiononphysicalandmechanicalpropertiesofparticleboardmadefrompomegranateprunings |