DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATION
Titanium alloy Ti-6Al-4V and AISI 304 stainless steel were diffusion bonded at various temperatures and holding times. The experimental investigation of the process parameters of the diffusion bonded coupons was carried out. Lap shear tests were performed to determine the strength of the joint, and...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Taylor's University
2015-10-01
|
| Series: | Journal of Engineering Science and Technology |
| Subjects: | |
| Online Access: | http://jestec.taylors.edu.my/Vol%2010%20Issue%2010%20October%202015/Volume%20(10)%20Issue%20(10)%201342-1349.pdf |
| _version_ | 1818495949174996992 |
|---|---|
| author | M. BALASUBRAMANIAN G. RAMESH V. BALASUBRAMANIAN |
| author_facet | M. BALASUBRAMANIAN G. RAMESH V. BALASUBRAMANIAN |
| author_sort | M. BALASUBRAMANIAN |
| collection | DOAJ |
| description | Titanium alloy Ti-6Al-4V and AISI 304 stainless steel were diffusion bonded at various temperatures and holding times. The experimental investigation of the process parameters of the diffusion bonded coupons was carried out. Lap shear tests were performed to determine the strength of the joint, and hardness
measurements were taken to understand the hardness in the diffusion region. Diffusion bonding was performed from the lower temperature to the higher temperature considering melting point of the parent material. Hardness measurement at the diffusion layer is almost equal to the parent material. Optical microscopy examination was carried out to determine the quality of the joint and XRD analysis was carried out to confirm the formation of
intermetallic compounds. The highest lap shear strength of 138.3 MPa was obtained at 800˚C at 60min holding time under 5 MPa pressure. |
| first_indexed | 2024-12-10T18:27:15Z |
| format | Article |
| id | doaj.art-faca5a777ba942948bf2822f5b6e412a |
| institution | Directory Open Access Journal |
| issn | 1823-4690 |
| language | English |
| last_indexed | 2024-12-10T18:27:15Z |
| publishDate | 2015-10-01 |
| publisher | Taylor's University |
| record_format | Article |
| series | Journal of Engineering Science and Technology |
| spelling | doaj.art-faca5a777ba942948bf2822f5b6e412a2022-12-22T01:38:02ZengTaylor's UniversityJournal of Engineering Science and Technology1823-46902015-10-01101013421349DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATIONM. BALASUBRAMANIAN0G. RAMESH1V. BALASUBRAMANIAN2Department of Mechanical Engineering, RMKCET,Puduvoyal, Tamilnadu, India Department of Mechanical Engineering, Velammal Engg College, Chennai, India Department of Manufacturing Engineering, Annamalai University, Chidambaram, India Titanium alloy Ti-6Al-4V and AISI 304 stainless steel were diffusion bonded at various temperatures and holding times. The experimental investigation of the process parameters of the diffusion bonded coupons was carried out. Lap shear tests were performed to determine the strength of the joint, and hardness measurements were taken to understand the hardness in the diffusion region. Diffusion bonding was performed from the lower temperature to the higher temperature considering melting point of the parent material. Hardness measurement at the diffusion layer is almost equal to the parent material. Optical microscopy examination was carried out to determine the quality of the joint and XRD analysis was carried out to confirm the formation of intermetallic compounds. The highest lap shear strength of 138.3 MPa was obtained at 800˚C at 60min holding time under 5 MPa pressure.http://jestec.taylors.edu.my/Vol%2010%20Issue%2010%20October%202015/Volume%20(10)%20Issue%20(10)%201342-1349.pdfTitanium alloy Ti-6Al-4VAISI 304 stainless steelDiffusion bondingMicrohardnessDiffusion layer |
| spellingShingle | M. BALASUBRAMANIAN G. RAMESH V. BALASUBRAMANIAN DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATION Journal of Engineering Science and Technology Titanium alloy Ti-6Al-4V AISI 304 stainless steel Diffusion bonding Microhardness Diffusion layer |
| title | DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATION |
| title_full | DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATION |
| title_fullStr | DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATION |
| title_full_unstemmed | DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATION |
| title_short | DIFFUSION BONDING OF TITANIUM ALLOY TI-6AL-4V AND AISI 304 STAINLESS STEEL – AN EXPERIMENTAL INVESTIGATION |
| title_sort | diffusion bonding of titanium alloy ti 6al 4v and aisi 304 stainless steel an experimental investigation |
| topic | Titanium alloy Ti-6Al-4V AISI 304 stainless steel Diffusion bonding Microhardness Diffusion layer |
| url | http://jestec.taylors.edu.my/Vol%2010%20Issue%2010%20October%202015/Volume%20(10)%20Issue%20(10)%201342-1349.pdf |
| work_keys_str_mv | AT mbalasubramanian diffusionbondingoftitaniumalloyti6al4vandaisi304stainlesssteelanexperimentalinvestigation AT gramesh diffusionbondingoftitaniumalloyti6al4vandaisi304stainlesssteelanexperimentalinvestigation AT vbalasubramanian diffusionbondingoftitaniumalloyti6al4vandaisi304stainlesssteelanexperimentalinvestigation |