Improvement of stress corrosion cracking resistance by low cycle fatigue of a CrNiMoV steel
Abstract Low cycle fatigue often interacts with stress corrosion cracking behavior. In this work, the effect of low cycle fatigue on stress corrosion cracking susceptibility of a CrNiMoV steel was investigated by interrupted fatigue tests in air and slow strain rate tensile tests in 3.5 wt% NaCl sol...