| Summary: | Simultaneous differential scanning calorimetry, DSC, and acoustic emission, AE, measurements were carried out for single crystals of quenched and stress-induced martensite stabilized (SIM-aged) shape memory Ni<sub>51</sub>Fe<sub>18</sub>Ga<sub>27</sub>Co<sub>4</sub> alloy. The transformation temperatures were shifted to higher values, the forward (from austenite to martensite) and reverse transitions became sharper and the width of the hysteresis increased in the SIM-aged sample. The energy distributions of acoustic hits showed similar behaviour to those of the quenched sample and the energy exponents, characterizing the power law behaviour, were also similar. For SIM-aged alloys at heating, in accordance with the sharper (burst-like) transition observed in the DSC run, few high-energy solitary hits were observed, and these hits did not fit to the energy distribution function fitted for smaller energies. Thus, these high-energy events were attributed to high sudden jumps in the phase transition during heating. The effect of long-range order (by applying a heat treatment at 573 K for 6 h to transform the B2 austenite to ordered L2<sub>1</sub> structure) and the SIM-aging on the transformation entropy was also investigated by DSC. It was found that the entropy was about 36% smaller after SIM-aging of the quenched sample and it was practically unchanged after austenite stabilization.
|
|---|