Improvement of Locally Produced Low- Density Polyethylene
In the present work, a polymer composite was fabricated by mixing LDPEwith different wt% of pigment (Fe2O3 and TiO2) to obtain desirable properties infabrication single screw-extruder was utilized , this mixing machine operated at atemperature between (150-170)Co.some of mechanical properties, such...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Unviversity of Technology- Iraq
2008-09-01
|
| Series: | Engineering and Technology Journal |
| Subjects: | |
| Online Access: | https://etj.uotechnology.edu.iq/article_26707_220e75f7234b66f41ed3253ebfb1fb91.pdf |
| _version_ | 1797325203092537344 |
|---|---|
| author | Najat .J.saleh Zanaib Y.shnean |
| author_facet | Najat .J.saleh Zanaib Y.shnean |
| author_sort | Najat .J.saleh |
| collection | DOAJ |
| description | In the present work, a polymer composite was fabricated by mixing LDPEwith different wt% of pigment (Fe2O3 and TiO2) to obtain desirable properties infabrication single screw-extruder was utilized , this mixing machine operated at atemperature between (150-170)Co.some of mechanical properties, such as tensile,impact, hardness and bending test were determined at different weight fraction ofcomposite materials. It was found that the addition of pigment (TiO2 and Fe2O3) to theLDPE leads to increase the modulus of elasticity, tensile strength, tensile strength atbreak, shore hardness on other hand it decreases the % elongation at break, and for theimpact strength. |
| first_indexed | 2024-03-08T06:07:10Z |
| format | Article |
| id | doaj.art-fe1bdcc14646450fad5b9b8a15bda3f0 |
| institution | Directory Open Access Journal |
| issn | 1681-6900 2412-0758 |
| language | English |
| last_indexed | 2024-03-08T06:07:10Z |
| publishDate | 2008-09-01 |
| publisher | Unviversity of Technology- Iraq |
| record_format | Article |
| series | Engineering and Technology Journal |
| spelling | doaj.art-fe1bdcc14646450fad5b9b8a15bda3f02024-02-04T17:53:16ZengUnviversity of Technology- IraqEngineering and Technology Journal1681-69002412-07582008-09-012691061106710.30684/etj.26.9.226707Improvement of Locally Produced Low- Density PolyethyleneNajat .J.salehZanaib Y.shnean0Dep. of Chemical Engineering, University of Technology-IraqIn the present work, a polymer composite was fabricated by mixing LDPEwith different wt% of pigment (Fe2O3 and TiO2) to obtain desirable properties infabrication single screw-extruder was utilized , this mixing machine operated at atemperature between (150-170)Co.some of mechanical properties, such as tensile,impact, hardness and bending test were determined at different weight fraction ofcomposite materials. It was found that the addition of pigment (TiO2 and Fe2O3) to theLDPE leads to increase the modulus of elasticity, tensile strength, tensile strength atbreak, shore hardness on other hand it decreases the % elongation at break, and for theimpact strength.https://etj.uotechnology.edu.iq/article_26707_220e75f7234b66f41ed3253ebfb1fb91.pdfldpeweatheringtio |
| spellingShingle | Najat .J.saleh Zanaib Y.shnean Improvement of Locally Produced Low- Density Polyethylene Engineering and Technology Journal ldpe weathering tio |
| title | Improvement of Locally Produced Low- Density Polyethylene |
| title_full | Improvement of Locally Produced Low- Density Polyethylene |
| title_fullStr | Improvement of Locally Produced Low- Density Polyethylene |
| title_full_unstemmed | Improvement of Locally Produced Low- Density Polyethylene |
| title_short | Improvement of Locally Produced Low- Density Polyethylene |
| title_sort | improvement of locally produced low density polyethylene |
| topic | ldpe weathering tio |
| url | https://etj.uotechnology.edu.iq/article_26707_220e75f7234b66f41ed3253ebfb1fb91.pdf |
| work_keys_str_mv | AT najatjsaleh improvementoflocallyproducedlowdensitypolyethylene AT zanaibyshnean improvementoflocallyproducedlowdensitypolyethylene |