Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites.
The purpose of this study was to evaluate the shear bond strength (SBS) of orthodontic brackets bonded with two types of nano-composites in comparison to a conventional orthodontic composite.Sixty extracted human first premolars were randomly divided into 3 groups each containing 20 teeth. In group...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Tehran University of Medical Sciences
2013-10-01
|
| Series: | Frontiers in Dentistry |
| Subjects: | |
| Online Access: | https://jdt.tums.ac.ir/index.php/jdt/article/view/603 |
| _version_ | 1818199176058503168 |
|---|---|
| author | Javad Chalipa Mohammad Sadegh Ahmad Akhondi Sepideh Arab Mohammad Javad Kharrazifard Maryam Ahmadyar |
| author_facet | Javad Chalipa Mohammad Sadegh Ahmad Akhondi Sepideh Arab Mohammad Javad Kharrazifard Maryam Ahmadyar |
| author_sort | Javad Chalipa |
| collection | DOAJ |
| description | The purpose of this study was to evaluate the shear bond strength (SBS) of orthodontic brackets bonded with two types of nano-composites in comparison to a conventional orthodontic composite.Sixty extracted human first premolars were randomly divided into 3 groups each containing 20 teeth. In group I, a conventional orthodontic composite (Transbond XT) was used to bond the brackets, while two nano-composites (Filtek TM Supreme XT and AELITE Aesthetic Enamel) were used in groups II and III respectively. The teeth were stored in distilled water at 37°C for 24 hours, thermocycled in distilled water and debonded with a universal testing machine at a crosshead speed of 1 mm/min. The adhesive remnant index (ARI) was also evaluated using a stereomicroscope.AELITE Aesthetic Enamel nano-composite revealed a SBS value of 8.44±2.09 MPa, which was higher than Transbond XT (6.91±2.13) and Filtek TM Supreme XT (6.04±2.01). Statistical analysis revealed a significant difference between groups II and III (P < 0.05). No significant difference was found between groups I and III, and between groups I and II (P > 0.05). Evaluation of ARI showed that Transbond XT left fewer adhesive remains on teeth after debonding.Results of this study indicate that the aforementioned nano-composites can be successfully used for bonding orthodontic brackets. |
| first_indexed | 2024-12-12T02:17:36Z |
| format | Article |
| id | doaj.art-ff06ebb0f32f4aa48a60645820c1458a |
| institution | Directory Open Access Journal |
| issn | 2676-296X |
| language | English |
| last_indexed | 2024-12-12T02:17:36Z |
| publishDate | 2013-10-01 |
| publisher | Tehran University of Medical Sciences |
| record_format | Article |
| series | Frontiers in Dentistry |
| spelling | doaj.art-ff06ebb0f32f4aa48a60645820c1458a2022-12-22T00:41:46ZengTehran University of Medical SciencesFrontiers in Dentistry2676-296X2013-10-01105Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites.Javad Chalipa0Mohammad Sadegh Ahmad Akhondi1Sepideh Arab2Mohammad Javad Kharrazifard3Maryam Ahmadyar4Assistant Professor, Department of Orthodontics, Tehran University of Medical Sciences, Tehran, Iran.Professor, Dental Research Center, Dentistry Research Institute, Department of Orthodontics, Tehran University of Medical Sciences, Tehran, Iran.Assistant Professor, Department of Orthodontics, Qazvin University of Medical Sciences, Qazvin, Iran.Post Graduated Student of Epidemiology, Dental Research Center, Tehran University of Medical Sciences, Tehran, Iran.General Dental Practitioner, Tehran, Iran.The purpose of this study was to evaluate the shear bond strength (SBS) of orthodontic brackets bonded with two types of nano-composites in comparison to a conventional orthodontic composite.Sixty extracted human first premolars were randomly divided into 3 groups each containing 20 teeth. In group I, a conventional orthodontic composite (Transbond XT) was used to bond the brackets, while two nano-composites (Filtek TM Supreme XT and AELITE Aesthetic Enamel) were used in groups II and III respectively. The teeth were stored in distilled water at 37°C for 24 hours, thermocycled in distilled water and debonded with a universal testing machine at a crosshead speed of 1 mm/min. The adhesive remnant index (ARI) was also evaluated using a stereomicroscope.AELITE Aesthetic Enamel nano-composite revealed a SBS value of 8.44±2.09 MPa, which was higher than Transbond XT (6.91±2.13) and Filtek TM Supreme XT (6.04±2.01). Statistical analysis revealed a significant difference between groups II and III (P < 0.05). No significant difference was found between groups I and III, and between groups I and II (P > 0.05). Evaluation of ARI showed that Transbond XT left fewer adhesive remains on teeth after debonding.Results of this study indicate that the aforementioned nano-composites can be successfully used for bonding orthodontic brackets.https://jdt.tums.ac.ir/index.php/jdt/article/view/603Bond StrengthCompositeNanoShear |
| spellingShingle | Javad Chalipa Mohammad Sadegh Ahmad Akhondi Sepideh Arab Mohammad Javad Kharrazifard Maryam Ahmadyar Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites. Frontiers in Dentistry Bond Strength Composite Nano Shear |
| title | Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites. |
| title_full | Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites. |
| title_fullStr | Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites. |
| title_full_unstemmed | Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites. |
| title_short | Evaluation of shear bond strength of orthodontic brackets bonded with nano-filled composites. |
| title_sort | evaluation of shear bond strength of orthodontic brackets bonded with nano filled composites |
| topic | Bond Strength Composite Nano Shear |
| url | https://jdt.tums.ac.ir/index.php/jdt/article/view/603 |
| work_keys_str_mv | AT javadchalipa evaluationofshearbondstrengthoforthodonticbracketsbondedwithnanofilledcomposites AT mohammadsadeghahmadakhondi evaluationofshearbondstrengthoforthodonticbracketsbondedwithnanofilledcomposites AT sepideharab evaluationofshearbondstrengthoforthodonticbracketsbondedwithnanofilledcomposites AT mohammadjavadkharrazifard evaluationofshearbondstrengthoforthodonticbracketsbondedwithnanofilledcomposites AT maryamahmadyar evaluationofshearbondstrengthoforthodonticbracketsbondedwithnanofilledcomposites |