SnSe + Ag₂Se composite engineering with ball milling for enhanced thermoelectric performance
Earth-abundant IV–VI semiconductor SnSe is regarded as a promising thermoelectric material due to its intrinsic low thermal conductivity. In this report, the highly textured SnSe/Ag2Se composites were first designed by solid solution method followed by spark plasma sintering (SPS) and their thermoel...
| Main Authors: | , , , , |
|---|---|
| Other Authors: | |
| Format: | Article |
| Language: | English |
| Published: |
Nonferrous Metals Society of China
2018
|
| Online Access: | http://hdl.handle.net/1721.1/117116 https://orcid.org/0000-0002-7841-8058 |
| Summary: | Earth-abundant IV–VI semiconductor SnSe is regarded as a promising thermoelectric material due to its intrinsic low thermal conductivity. In this report, the highly textured SnSe/Ag2Se composites were first designed by solid solution method followed by spark plasma sintering (SPS) and their thermoelectric properties in two directions were investigated, and then, the performance of composites was further optimized with an additional ball milling. The coexistence of SnSe and Ag2Se phases is clearly confirmed by energy-dispersive X-ray spectroscopy (EDX) in transmission electron microscopy (TEM). After ball milling, the size of SnSe grains as well as the incorporated Ag2Se particles reduces effectively, which synergistically optimizes the electrical and thermal transport properties at high temperature range. As a result, a maximum ZT of ~ 0.74 at 773 K for SnSe + 1.0%Ag2Se in the direction vertical to the pressing direction is achieved. Composite engineering with additional ball milling is thus proved to be an efficient way to improve the thermoelectric properties of SnSe, and this strategy could be applicable to other thermoelectric systems. |
|---|