Separation and purification of Si from Sn-30Si alloy by electromagnetic semi-continuous directional solidification
Electromagnetic semi-continuous directional solidification (ESCDS) was employed to separate and purify Si from Sn-30Si alloy. The experimental results indicate that the enrichment of primary silicon reaches approximately 91% as the solidification rate is 1.5 mm/min high. While Ca and B are removed b...
Main Authors: | Huang, Feng, Zhao, Lian, Liu, Lin, Hu, Zhili, Chen, Ruirun, Dong, Zhili |
---|---|
Other Authors: | School of Materials Science and Engineering |
Format: | Journal Article |
Language: | English |
Published: |
2020
|
Subjects: | |
Online Access: | https://hdl.handle.net/10356/143853 |
Similar Items
-
Removal of Fe impurities from Al alloy scraps by electromagnetic directional solidification combined with Si addition
by: Yakun Zhang, et al.
Published: (2023-09-01) -
Controlling Segregation Behavior of Primary Si in Hypereutectic Al-Si Alloy by Electromagnetic Stirring
by: Qingchuan Zou, et al.
Published: (2020-08-01) -
Investigation of solidification behavior of the Sn-rich ternary Sn–Bi–Zn alloys
by: S Mladenović, et al.
Published: (2017-03-01) -
Solidification Simulation of Al-Si Alloys with Dendrite Tip Undercooling
by: Hongda Wang, et al.
Published: (2022-03-01) -
Continuous melting and directional solidification of silicon ingot with an electromagnetic cold crucible
by: Huang Feng, et al.
Published: (2012-02-01)