High deformation process of Al-Li alloy composites with Cu-coated SiC particles
This project involved the processing of Al-Li based metal matrix composites reinforced with Cu-coated SiCp. A high deformation process was adopted where conventional tumbling mixing was followed by cold isostatic pressing (CIP). The green compact was then hot pressed and hot extruded, at 530°C and 5...
| Tác giả chính: | |
|---|---|
| Tác giả khác: | |
| Định dạng: | Luận văn |
| Ngôn ngữ: | English |
| Được phát hành: |
2009
|
| Những chủ đề: | |
| Truy cập trực tuyến: | http://hdl.handle.net/10356/19931 |
| _version_ | 1826120739026108416 |
|---|---|
| author | Cao, Yahui |
| author2 | Boey, Freddy Yin Chiang |
| author_facet | Boey, Freddy Yin Chiang Cao, Yahui |
| author_sort | Cao, Yahui |
| collection | NTU |
| description | This project involved the processing of Al-Li based metal matrix composites reinforced with Cu-coated SiCp. A high deformation process was adopted where conventional tumbling mixing was followed by cold isostatic pressing (CIP). The green compact was then hot pressed and hot extruded, at 530°C and 510°C respectively. Hot isostatic pressing (HIP) was employed as a post consolidation step for the extruded rods. After being treated at T6 condition, the samples were tested by 3-point bending mode dynamically and statically. |
| first_indexed | 2024-10-01T05:21:22Z |
| format | Thesis |
| id | ntu-10356/19931 |
| institution | Nanyang Technological University |
| language | English |
| last_indexed | 2024-10-01T05:21:22Z |
| publishDate | 2009 |
| record_format | dspace |
| spelling | ntu-10356/199312023-03-11T16:55:29Z High deformation process of Al-Li alloy composites with Cu-coated SiC particles Cao, Yahui Boey, Freddy Yin Chiang School of Mechanical and Production Engineering DRNTU::Engineering::Materials::Composite materials This project involved the processing of Al-Li based metal matrix composites reinforced with Cu-coated SiCp. A high deformation process was adopted where conventional tumbling mixing was followed by cold isostatic pressing (CIP). The green compact was then hot pressed and hot extruded, at 530°C and 510°C respectively. Hot isostatic pressing (HIP) was employed as a post consolidation step for the extruded rods. After being treated at T6 condition, the samples were tested by 3-point bending mode dynamically and statically. Master of Science 2009-12-14T07:51:52Z 2009-12-14T07:51:52Z 1997 1997 Thesis http://hdl.handle.net/10356/19931 en NANYANG TECHNOLOGICAL UNIVERSITY 130 p. application/pdf |
| spellingShingle | DRNTU::Engineering::Materials::Composite materials Cao, Yahui High deformation process of Al-Li alloy composites with Cu-coated SiC particles |
| title | High deformation process of Al-Li alloy composites with Cu-coated SiC particles |
| title_full | High deformation process of Al-Li alloy composites with Cu-coated SiC particles |
| title_fullStr | High deformation process of Al-Li alloy composites with Cu-coated SiC particles |
| title_full_unstemmed | High deformation process of Al-Li alloy composites with Cu-coated SiC particles |
| title_short | High deformation process of Al-Li alloy composites with Cu-coated SiC particles |
| title_sort | high deformation process of al li alloy composites with cu coated sic particles |
| topic | DRNTU::Engineering::Materials::Composite materials |
| url | http://hdl.handle.net/10356/19931 |
| work_keys_str_mv | AT caoyahui highdeformationprocessofallialloycompositeswithcucoatedsicparticles |