Fracture mechanics investigation for a 3-D crack in a MRT rail
Fatigue crack growth has always been a concern for railways as it might lead to derailment which causes catastrophic consequences. When the crack is subjected to cyclic rolling contact due to regular movement of the trains, the rate of crack growth greatly increases. Although there were several stud...
Main Author: | Lim, Yu Heng |
---|---|
Other Authors: | Xiao Zhongmin |
Format: | Final Year Project (FYP) |
Language: | English |
Published: |
2018
|
Subjects: | |
Online Access: | http://hdl.handle.net/10356/74317 |
Similar Items
-
Fatigue failure investigation in MRT rails with an internal crack
by: Cheong, Xiang Shun
Published: (2019) -
Investigation on fatigue crack growth in MRT rail Part I - surface crack case
by: Ko, Ming Chan
Published: (2018) -
On the fracture toughness study of Singapore MRT rails with 3D edge cracks : multiple cracks behaviours of the railway wheel due to cyclic rolling contact
by: Myat, Noe Oo
Published: (2019) -
3-D fatigue crack study in the rail
by: Chen, Xiaoyong
Published: (2018) -
Analysis of departure time choice behaviour of MRT commuters
by: Lim, Clara ShiJun.
Published: (2013)