Structure, ferroelectric and piezoelectric properties of multiferroic Bi0.875Sm0.125FeO3 ceramics
With a rhombohedra-like structure, the Bi0.875Sm0.125FeO3 ceramics show much-improved ferroelectric and piezoelectric properties: a saturated ferroelectric polarization of 40 μC/cm2 and a piezoelectric d33 of 45 pC/N at 20 °C. After the polarized sample was annealed at 600 °C, its d33 decreases to ∼...
Main Authors: | Chen, Xiaomin, Wang, Junling, Yuan, Guoliang, Wu, Di, Liu, Junming, Yin, Jiang, Liu, Zhiguo |
---|---|
Other Authors: | School of Materials Science & Engineering |
Format: | Journal Article |
Language: | English |
Published: |
2013
|
Online Access: | https://hdl.handle.net/10356/96831 http://hdl.handle.net/10220/11640 |
Similar Items
-
Observation of 3D Heisenberg-like ferromagnetism in single crystal
La_{0.875}Sr_{0.125}MnO_3
by: Nair, S, et al.
Published: (2003) -
Catalytic Oxidation Mechanism of Toluene on the Ce<sub>0.875</sub>Zr<sub>0.125</sub>O<sub>2</sub> (110) Surface
by: Yuning Leng, et al.
Published: (2023-12-01) -
Oxygen-vacancy-induced atomic and electronic reconstructions in magnetic Sr(Ti0.875Fe0.125)O3-δ thin films
by: Yi Liang, et al.
Published: (2020-01-01) -
Carbon Monoxide and Propylene Catalytic Oxidation Activity of Noble Metals (M = Pt, Pd, Ag, and Au) Loaded on the Surface of Ce<sub>0.875</sub>Zr<sub>0.125</sub>O<sub>2</sub> (110)
by: Chenxi Zhang, et al.
Published: (2023-12-01) -
Structure and piezoelectric properties of BiFeO3 and Bi0.92Dy0.08FeO3 multiferroics at high temperature
by: Sun, Chen, et al.
Published: (2013)