TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER
HRS-WC mixture having asymmetric gradation causes pores of mixture opened wider, so it causes oxidation on the asphalt mixture. In order to solve the problem, filler was applied to fill up the pores in the mixture since it can increase its flexibility and durability.. In the research crumb rubber wa...
| Main Authors: | , |
|---|---|
| Format: | Thesis |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2012
|
| Subjects: |
| _version_ | 1797032965071437824 |
|---|---|
| author | , Nurhidayat Delfianto , Dr. Ir. Latif Budi Suparma, M.Sc., |
| author_facet | , Nurhidayat Delfianto , Dr. Ir. Latif Budi Suparma, M.Sc., |
| author_sort | , Nurhidayat Delfianto |
| collection | UGM |
| description | HRS-WC mixture having asymmetric gradation causes pores of mixture
opened wider, so it causes oxidation on the asphalt mixture. In order to solve the
problem, filler was applied to fill up the pores in the mixture since it can increase its
flexibility and durability.. In the research crumb rubber was used as substitute of
filler. By using crumb rubber, it is expected that durability and stability of mixture as
well as Indirect Tensile Strength of HRS-WC mixture will be obtained when it is
submerged at 60oC during 2, 4, 7 and 14 days.
The research used four variations of crumb rubber content 0%, 5%, 10% and
15%. The durability test was conducted using Marshall test apparatus and the ITS
test used modified Marshall apparatus on the submersion of 2, 4, 7 and 14 days at
60oC. For ITS, preparation of dry samples and samples conditioning were conducted
in advance to make them saturated.
It was reported that the stability of samples submerged during 2 - 14 days
with the crumb rubber content 0% are 1449 kg, 1215 kg 1141 kg and 1136 kg |
| first_indexed | 2024-03-13T22:46:49Z |
| format | Thesis |
| id | oai:generic.eprints.org:118511 |
| institution | Universiti Gadjah Mada |
| last_indexed | 2024-03-13T22:46:49Z |
| publishDate | 2012 |
| publisher | [Yogyakarta] : Universitas Gadjah Mada |
| record_format | dspace |
| spelling | oai:generic.eprints.org:1185112016-03-04T08:48:07Z https://repository.ugm.ac.id/118511/ TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER , Nurhidayat Delfianto , Dr. Ir. Latif Budi Suparma, M.Sc., ETD HRS-WC mixture having asymmetric gradation causes pores of mixture opened wider, so it causes oxidation on the asphalt mixture. In order to solve the problem, filler was applied to fill up the pores in the mixture since it can increase its flexibility and durability.. In the research crumb rubber was used as substitute of filler. By using crumb rubber, it is expected that durability and stability of mixture as well as Indirect Tensile Strength of HRS-WC mixture will be obtained when it is submerged at 60oC during 2, 4, 7 and 14 days. The research used four variations of crumb rubber content 0%, 5%, 10% and 15%. The durability test was conducted using Marshall test apparatus and the ITS test used modified Marshall apparatus on the submersion of 2, 4, 7 and 14 days at 60oC. For ITS, preparation of dry samples and samples conditioning were conducted in advance to make them saturated. It was reported that the stability of samples submerged during 2 - 14 days with the crumb rubber content 0% are 1449 kg, 1215 kg 1141 kg and 1136 kg [Yogyakarta] : Universitas Gadjah Mada 2012 Thesis NonPeerReviewed , Nurhidayat Delfianto and , Dr. Ir. Latif Budi Suparma, M.Sc., (2012) TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER. UNSPECIFIED thesis, UNSPECIFIED. http://etd.ugm.ac.id/index.php?mod=penelitian_detail&sub=PenelitianDetail&act=view&typ=html&buku_id=58484 |
| spellingShingle | ETD , Nurhidayat Delfianto , Dr. Ir. Latif Budi Suparma, M.Sc., TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER |
| title | TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER |
| title_full | TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER |
| title_fullStr | TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER |
| title_full_unstemmed | TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER |
| title_short | TINJAUAN DURABILITAS CAMPURAN HRS-WC YANG MENGGUNAKAN LIMBAH CRUMB RUBBER SEBAGAI PENGGANTI FILLER |
| title_sort | tinjauan durabilitas campuran hrs wc yang menggunakan limbah crumb rubber sebagai pengganti filler |
| topic | ETD |
| work_keys_str_mv | AT nurhidayatdelfianto tinjauandurabilitascampuranhrswcyangmenggunakanlimbahcrumbrubbersebagaipenggantifiller AT drirlatifbudisuparmamsc tinjauandurabilitascampuranhrswcyangmenggunakanlimbahcrumbrubbersebagaipenggantifiller |