PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT
The research of mixture of palm oil by using variation of mixture of Ni/AlMCM-41, H-AlMCM-41 and bentonite has been conducted. The purpose of this research was to identify the effect of bentonite on catalyst mixture of Ni/AlMCM-41 and H-AlMCM-41. For the synthesis of AlMCM-41, cetyltrimetilamonium b...
| Main Authors: | , |
|---|---|
| Format: | Thesis |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2013
|
| Subjects: |
| _version_ | 1797034755252813824 |
|---|---|
| author | , GIUR MUHAMMAD SATRIA , Prof. Dr. Iip Izul Falah |
| author_facet | , GIUR MUHAMMAD SATRIA , Prof. Dr. Iip Izul Falah |
| author_sort | , GIUR MUHAMMAD SATRIA |
| collection | UGM |
| description | The research of mixture of palm oil by using variation of mixture of
Ni/AlMCM-41, H-AlMCM-41 and bentonite has been conducted. The purpose of
this research was to identify the effect of bentonite on catalyst mixture of
Ni/AlMCM-41 and H-AlMCM-41.
For the synthesis of AlMCM-41, cetyltrimetilamonium bromide (CTAB)
and tetramethylammonium hydroxide (TMAOH) were used as a template, sodium
silicate as a source of silica, and sodium aluminate as a source of aluminum.
Crystallization was carried out hydrothermally at a temperature of 90
o
C for 36
hours and calcined at 540
o
C for 6 hours. The AlMCM-41 was analyzed using Xray
diffraction (XRD) and infrared spectrophotometry (FTIR) methods.
Ni/AlMCM-41 was made by soaking AlMCM-41 into NiCl2 solution. After
filtering, it was dried and than reduced at 450
o
C. Its surface area was analyzed
using nitrogen adsorption method and its shape was shown by Transmission
Electron Microscopy (TEM) image. H-AlMCM-41 was made by soaking
AlMCM-41 into NH4Cl solution, calcined at 540
o
C. The acidities of AlMCM-41,
H-AlMCM-41, and Ni/AlMCM-41 are determined by adsorption of ammonia and
pyridine methods. Palm oil cracking was conducted using catalysts of mixture of
H-AlMCM-41 and bentonite |
| first_indexed | 2024-03-13T23:16:47Z |
| format | Thesis |
| id | oai:generic.eprints.org:127319 |
| institution | Universiti Gadjah Mada |
| last_indexed | 2024-03-13T23:16:47Z |
| publishDate | 2013 |
| publisher | [Yogyakarta] : Universitas Gadjah Mada |
| record_format | dspace |
| spelling | oai:generic.eprints.org:1273192016-03-04T08:37:50Z https://repository.ugm.ac.id/127319/ PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT , GIUR MUHAMMAD SATRIA , Prof. Dr. Iip Izul Falah ETD The research of mixture of palm oil by using variation of mixture of Ni/AlMCM-41, H-AlMCM-41 and bentonite has been conducted. The purpose of this research was to identify the effect of bentonite on catalyst mixture of Ni/AlMCM-41 and H-AlMCM-41. For the synthesis of AlMCM-41, cetyltrimetilamonium bromide (CTAB) and tetramethylammonium hydroxide (TMAOH) were used as a template, sodium silicate as a source of silica, and sodium aluminate as a source of aluminum. Crystallization was carried out hydrothermally at a temperature of 90 o C for 36 hours and calcined at 540 o C for 6 hours. The AlMCM-41 was analyzed using Xray diffraction (XRD) and infrared spectrophotometry (FTIR) methods. Ni/AlMCM-41 was made by soaking AlMCM-41 into NiCl2 solution. After filtering, it was dried and than reduced at 450 o C. Its surface area was analyzed using nitrogen adsorption method and its shape was shown by Transmission Electron Microscopy (TEM) image. H-AlMCM-41 was made by soaking AlMCM-41 into NH4Cl solution, calcined at 540 o C. The acidities of AlMCM-41, H-AlMCM-41, and Ni/AlMCM-41 are determined by adsorption of ammonia and pyridine methods. Palm oil cracking was conducted using catalysts of mixture of H-AlMCM-41 and bentonite [Yogyakarta] : Universitas Gadjah Mada 2013 Thesis NonPeerReviewed , GIUR MUHAMMAD SATRIA and , Prof. Dr. Iip Izul Falah (2013) PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT. UNSPECIFIED thesis, UNSPECIFIED. http://etd.ugm.ac.id/index.php?mod=penelitian_detail&sub=PenelitianDetail&act=view&typ=html&buku_id=67569 |
| spellingShingle | ETD , GIUR MUHAMMAD SATRIA , Prof. Dr. Iip Izul Falah PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT |
| title | PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT |
| title_full | PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT |
| title_fullStr | PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT |
| title_full_unstemmed | PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT |
| title_short | PERENGKAHAN MINYAK KELAPA SAWIT MENGGUNAKAN VARIASI CAMPURAN KATALIS Ni/AlMCM-41, H-AlMCM-41 DAN BENTONIT |
| title_sort | perengkahan minyak kelapa sawit menggunakan variasi campuran katalis ni almcm 41 h almcm 41 dan bentonit |
| topic | ETD |
| work_keys_str_mv | AT giurmuhammadsatria perengkahanminyakkelapasawitmenggunakanvariasicampurankatalisnialmcm41halmcm41danbentonit AT profdriipizulfalah perengkahanminyakkelapasawitmenggunakanvariasicampurankatalisnialmcm41halmcm41danbentonit |