PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING
Fiber Polyvinyl Alcohol (PVA) containing Fe3O4 nanoparticles have been successfully prepared by the method electrospining. The fiber is made from a mixture solution of Fe3O4 nanoparticles in a solution of 10% PVA with a weight ratio of 10%, 50% and 70%. Electrospining process done at the needle tip...
| Main Authors: | , |
|---|---|
| Format: | Thesis |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2014
|
| Subjects: |
| _version_ | 1826048445704568832 |
|---|---|
| author | , ANITA FIRA WALUYO , Dr. Harsojo |
| author_facet | , ANITA FIRA WALUYO , Dr. Harsojo |
| author_sort | , ANITA FIRA WALUYO |
| collection | UGM |
| description | Fiber Polyvinyl Alcohol (PVA) containing Fe3O4 nanoparticles have been
successfully prepared by the method electrospining. The fiber is made from a mixture
solution of Fe3O4 nanoparticles in a solution of 10% PVA with a weight ratio of 10%,
50% and 70%. Electrospining process done at the needle tip from collector distance
of 15cm with 15kV voltage. Fe3O4 particles bond with PVA known from testing
Fourier Transform Infrared (FT-IR). Test results spectrometer Ultra Violet Visible
(UV-Vis) by simply using Visible light with a wavelength of 400-700 nm, indicating
higher absorption values with increasing concentration of Fe3O4 in fiber. Analysis of
Scanning Electron Microscopy (SEM) of each variation of the mass ratio suggests
that the higher the ratio of the mass effect on fiber diameter were also greater (with a
diameter range of 100-300 nm). The calculation of the size of the diameter of the
crystal using the Scherrer equation from the X-Ray Diffraction (XRD) show that the
Fe3O4 crystal fiber has filled in the smaller sizes (19±1 nm) than in the state of
powder (20±2 nm). Analysis of Transmission Electron Microscopy (TEM) show that
the Fe3O4 particles 16±8 nm has a larger size, when loaded in fiber (which is 25±10
nm), than in powder form because of agglomeration. Vibrating Sample
Magnetometer Analysis (VSM) show that the fiber samples (Fe3O4/PVA) are
superparamagnetic with following results: saturation magnetization (Ms), coercivity
field (Hc) and remanent magnetization (Mr) ie Ms=83,08 emu/g, Hc=0,07 kOe and Mr
=26 emu/g compared with a sample of Fe3O4 particles that Ms = 29.45 emu/g, Hc =
0.05 kOe and Mr = 8.62 emu/g. This behaviour is caused by the presence of PVA that
wrap Fe3O4 particles.
Keywords: Electrospinning, Fibers, Magnetite (Fe3O4), Polyvinyl Alcohol |
| first_indexed | 2024-03-13T23:29:41Z |
| format | Thesis |
| id | oai:generic.eprints.org:130557 |
| institution | Universiti Gadjah Mada |
| last_indexed | 2024-03-13T23:29:41Z |
| publishDate | 2014 |
| publisher | [Yogyakarta] : Universitas Gadjah Mada |
| record_format | dspace |
| spelling | oai:generic.eprints.org:1305572016-03-04T07:52:20Z https://repository.ugm.ac.id/130557/ PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING , ANITA FIRA WALUYO , Dr. Harsojo ETD Fiber Polyvinyl Alcohol (PVA) containing Fe3O4 nanoparticles have been successfully prepared by the method electrospining. The fiber is made from a mixture solution of Fe3O4 nanoparticles in a solution of 10% PVA with a weight ratio of 10%, 50% and 70%. Electrospining process done at the needle tip from collector distance of 15cm with 15kV voltage. Fe3O4 particles bond with PVA known from testing Fourier Transform Infrared (FT-IR). Test results spectrometer Ultra Violet Visible (UV-Vis) by simply using Visible light with a wavelength of 400-700 nm, indicating higher absorption values with increasing concentration of Fe3O4 in fiber. Analysis of Scanning Electron Microscopy (SEM) of each variation of the mass ratio suggests that the higher the ratio of the mass effect on fiber diameter were also greater (with a diameter range of 100-300 nm). The calculation of the size of the diameter of the crystal using the Scherrer equation from the X-Ray Diffraction (XRD) show that the Fe3O4 crystal fiber has filled in the smaller sizes (19±1 nm) than in the state of powder (20±2 nm). Analysis of Transmission Electron Microscopy (TEM) show that the Fe3O4 particles 16±8 nm has a larger size, when loaded in fiber (which is 25±10 nm), than in powder form because of agglomeration. Vibrating Sample Magnetometer Analysis (VSM) show that the fiber samples (Fe3O4/PVA) are superparamagnetic with following results: saturation magnetization (Ms), coercivity field (Hc) and remanent magnetization (Mr) ie Ms=83,08 emu/g, Hc=0,07 kOe and Mr =26 emu/g compared with a sample of Fe3O4 particles that Ms = 29.45 emu/g, Hc = 0.05 kOe and Mr = 8.62 emu/g. This behaviour is caused by the presence of PVA that wrap Fe3O4 particles. Keywords: Electrospinning, Fibers, Magnetite (Fe3O4), Polyvinyl Alcohol [Yogyakarta] : Universitas Gadjah Mada 2014 Thesis NonPeerReviewed , ANITA FIRA WALUYO and , Dr. Harsojo (2014) PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING. UNSPECIFIED thesis, UNSPECIFIED. http://etd.ugm.ac.id/index.php?mod=penelitian_detail&sub=PenelitianDetail&act=view&typ=html&buku_id=70982 |
| spellingShingle | ETD , ANITA FIRA WALUYO , Dr. Harsojo PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING |
| title | PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING |
| title_full | PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING |
| title_fullStr | PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING |
| title_full_unstemmed | PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING |
| title_short | PEMBUATAN DAN KARAKTERISASI FIBER PVA YANG MEMUAT SUPERPARAMAGNETIK FE3O4 DENGAN METODE ELEKTROSPINING |
| title_sort | pembuatan dan karakterisasi fiber pva yang memuat superparamagnetik fe3o4 dengan metode elektrospining |
| topic | ETD |
| work_keys_str_mv | AT anitafirawaluyo pembuatandankarakterisasifiberpvayangmemuatsuperparamagnetikfe3o4denganmetodeelektrospining AT drharsojo pembuatandankarakterisasifiberpvayangmemuatsuperparamagnetikfe3o4denganmetodeelektrospining |