STUDI PENGARUH UKURAN BUTIR PARTIKEL DAN STRUKTUR KRISTAL TERHADAP SIFAT DIELEKTRIK NANOPARTIKEL COBALT FERRITE (CoFe2O4)
Cobalt Ferrite (CoFe2O4) has been synthesized with various grain size of particle of 4.3 nm, 7.7 nm, 8.7 nm, 9.0 nm and 9.7 nm using coprecipitation methods then the result was pressed with 50.000N of force to be pellet with diameter of 1 2.26 mm. The measurement uses computerized impedan...
Main Authors: | , RAHMAT WIDODO, , Dr. Edi Suharyadi, M.Eng |
---|---|
Format: | Thesis |
Published: |
[Yogyakarta] : Universitas Gadjah Mada
2014
|
Subjects: |
Similar Items
-
KAJIAN SIFAT DIELEKTRIK PADA NANOPARTIKEL COBALT FERRITE (CoFe2O4) YANG DIENKAPSULASI DENGAN POLYETHYLENE GLYCOL (PEG-4000)
by: , AJO DIAN YUSANDIKA, et al.
Published: (2014) -
FABRIKASI DAN KARAKTERISASI STRUKTUR KRISTAL DAN SIFAT KEMAGNETAN NANOPARTIKEL COBALT FERRITE (CoFe2O4) BESERTA PROSES FUNGSIONALISASINYA DENGAN PEG-4000
by: , Eko Arief Setiadi, et al.
Published: (2013) -
ANALISIS PENGARUH STRUKTUR KRISTAL TERHADAP TETAPAN SUSEPTIBILITAS PADA POLYETHYLENE GLYCOL (PEG-4000)-COATED NANOPARTIKEL MAGNETIK COBALT FERRITE (CoFe2O4)
by: , RIZKI EKA SISWANTO, et al.
Published: (2014) -
KAJIAN SIFAT KEMAGNETAN PADA NANOPARTIKEL COBALT FERRITE (CoFe2O4) YANG DIENKAPSULASI DENGAN POLYETHYLENE GLYKOL (PEG-4000) DAN SILIKA
by: , SULANJARI, et al.
Published: (2014) -
KAJIAN STRUKTUR KRISTAL DAN SIFAT KEMAGNETAN PADA NANOPARTIKEL MANGANESE FERRITE (MnFe2O4) DAN PROSES FUNGSIONALISASINYA DENGAN PEG-4000
by: , ROSITA D TAWAINELLA, et al.
Published: (2014)