Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa
The research purpose was to immobilize Sr-90 adsorbed by zeolite using cement and coconuts fiber. The research was pursued by varied % v/o of coconuts fiber and investigated their compressive strength, bending strength and leaching rate. The 13% v/o of zeolite was mixed with cement on 0.3 of water/c...
Main Author: | |
---|---|
Format: | Article |
Published: |
[Yogyakarta] : Universitas Gadjah Mada
2001
|
Subjects: |
_version_ | 1797017807392604160 |
---|---|
author | Perpustakaan UGM, i-lib |
author_facet | Perpustakaan UGM, i-lib |
author_sort | Perpustakaan UGM, i-lib |
collection | UGM |
description | The research purpose was to immobilize Sr-90 adsorbed by zeolite using cement and coconuts fiber. The research was pursued by varied % v/o of coconuts fiber and investigated their compressive strength, bending strength and leaching rate. The 13% v/o of zeolite was mixed with cement on 0.3 of water/cement weight ratio. The optimum composition of coconuts fiber causing increasing of mechanical strength has been founded at 0.50% v/o of fiber. The axial force resistance of fiber is higher than the radial one. The leaching rate of fiber reinforced mortar doesn't significantly change.
Key Words: Zeolite - cement and coconuts fiber |
first_indexed | 2024-03-13T18:35:50Z |
format | Article |
id | oai:generic.eprints.org:18383 |
institution | Universiti Gadjah Mada |
last_indexed | 2024-03-13T18:35:50Z |
publishDate | 2001 |
publisher | [Yogyakarta] : Universitas Gadjah Mada |
record_format | dspace |
spelling | oai:generic.eprints.org:183832014-06-18T00:32:41Z https://repository.ugm.ac.id/18383/ Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa Perpustakaan UGM, i-lib Jurnal i-lib UGM The research purpose was to immobilize Sr-90 adsorbed by zeolite using cement and coconuts fiber. The research was pursued by varied % v/o of coconuts fiber and investigated their compressive strength, bending strength and leaching rate. The 13% v/o of zeolite was mixed with cement on 0.3 of water/cement weight ratio. The optimum composition of coconuts fiber causing increasing of mechanical strength has been founded at 0.50% v/o of fiber. The axial force resistance of fiber is higher than the radial one. The leaching rate of fiber reinforced mortar doesn't significantly change. Key Words: Zeolite - cement and coconuts fiber [Yogyakarta] : Universitas Gadjah Mada 2001 Article NonPeerReviewed Perpustakaan UGM, i-lib (2001) Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa. Jurnal i-lib UGM. http://i-lib.ugm.ac.id/jurnal/download.php?dataId=1168 |
spellingShingle | Jurnal i-lib UGM Perpustakaan UGM, i-lib Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa |
title | Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa |
title_full | Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa |
title_fullStr | Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa |
title_full_unstemmed | Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa |
title_short | Imobilisasi sr-90 dalam zeolit dengan proses pemadatan semen-serat kelapa |
title_sort | imobilisasi sr 90 dalam zeolit dengan proses pemadatan semen serat kelapa |
topic | Jurnal i-lib UGM |
work_keys_str_mv | AT perpustakaanugmilib imobilisasisr90dalamzeolitdenganprosespemadatansemenseratkelapa |