| Summary: | The specimens of silane epoxy resins insulating materials are based on diglycidyl ether of bisphenol-A, cured with metaphenilene-diamine, with stochiometric value of unity, and 325-mesh silica filler treatment. Silane epoxy resins are the name of new thermosetting polymeric insulation materials that have been developed, the materials composition was obtained from the experimental research. To investigate the influence of the filler material the amount of six types of variation of the silane in the room temperature was vulcaniced, compared with the 6 types of variation of the filler without silane treatment. The study towards improving the performance of the epoxy resins was conducted, by adding silane treatment as filler, and a new performance with regard to hydrophobicity was realized. Experimental method for 12 types of specimens was carried out through the following procedure
|
|---|