This research aims to study microstructure of a HP micro alloy as a result of stress rupture test and observe dislocation-carbide precipitate interaction. Specimens were examined using Transmission Electron Microscope (TEM). The TEM observation showed that dislocations cut through carbide precipitat...
| Main Author: | |
|---|---|
| Format: | Article |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2005
|
| Subjects: |
| _version_ | 1826032220143353856 |
|---|---|
| author | Perpustakaan UGM, i-lib |
| author_facet | Perpustakaan UGM, i-lib |
| author_sort | Perpustakaan UGM, i-lib |
| collection | UGM |
| description | This research aims to study microstructure of a HP micro alloy as a result of stress rupture test and observe dislocation-carbide precipitate interaction. Specimens were examined using Transmission Electron Microscope (TEM). The TEM observation showed that dislocations cut through carbide precipitates on stress ruptured specimens. In addition, there is no evidence of the dislocation loops around the particles as expected from the Orowan mechanism.
Key words : HP Micro alloy, transmission electron microscope, stress rupture, carbide precipitate, dislocation. |
| first_indexed | 2024-03-13T18:50:10Z |
| format | Article |
| id | oai:generic.eprints.org:23255 |
| institution | Universiti Gadjah Mada |
| last_indexed | 2024-03-13T18:50:10Z |
| publishDate | 2005 |
| publisher | [Yogyakarta] : Universitas Gadjah Mada |
| record_format | dspace |
| spelling | oai:generic.eprints.org:232552014-06-18T00:27:34Z https://repository.ugm.ac.id/23255/ Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture Perpustakaan UGM, i-lib Jurnal i-lib UGM This research aims to study microstructure of a HP micro alloy as a result of stress rupture test and observe dislocation-carbide precipitate interaction. Specimens were examined using Transmission Electron Microscope (TEM). The TEM observation showed that dislocations cut through carbide precipitates on stress ruptured specimens. In addition, there is no evidence of the dislocation loops around the particles as expected from the Orowan mechanism. Key words : HP Micro alloy, transmission electron microscope, stress rupture, carbide precipitate, dislocation. [Yogyakarta] : Universitas Gadjah Mada 2005 Article NonPeerReviewed Perpustakaan UGM, i-lib (2005) Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture. Jurnal i-lib UGM. http://i-lib.ugm.ac.id/jurnal/download.php?dataId=6197 |
| spellingShingle | Jurnal i-lib UGM Perpustakaan UGM, i-lib Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture |
| title | Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture |
| title_full | Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture |
| title_fullStr | Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture |
| title_full_unstemmed | Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture |
| title_short | Studi Tem Pada Baja Tahan Karat Austenitik Grade HP Microalloy hasil Uji Stress Rupture |
| title_sort | studi tem pada baja tahan karat austenitik grade hp microalloy hasil uji stress rupture |
| topic | Jurnal i-lib UGM |
| work_keys_str_mv | AT perpustakaanugmilib studitempadabajatahankarataustenitikgradehpmicroalloyhasilujistressrupture |