Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding
The 10 mm thick Aluminum 6061 plates have been corner joined using varied design and those were 45ᴼ Corner Butt and Corner Lap Joints (CB-45 & CL). Friction tool was hardened EMS 45. True experimental method was used with independent parameters is feed rate which varied at 10 mm/min, 15 mm/min a...
| Main Authors: | , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://repository.ugm.ac.id/274684/1/matecconf_icet4sd2018_01106.pdf |
| _version_ | 1797036877650329600 |
|---|---|
| author | Setiawan, Widia Darmadi, Djarot B. Suprapto, Wahyono Soenoko, Rudy |
| author_facet | Setiawan, Widia Darmadi, Djarot B. Suprapto, Wahyono Soenoko, Rudy |
| author_sort | Setiawan, Widia |
| collection | UGM |
| description | The 10 mm thick Aluminum 6061 plates have been corner joined using varied design and those were 45ᴼ Corner Butt and Corner Lap Joints (CB-45 & CL). Friction tool was hardened EMS 45. True experimental method was used with independent parameters is feed rate which varied at 10 mm/min, 15 mm/min and 30 mm/min respectively. Other parameter such as rotating speed was kept constant. Experiment results show that, CB-45 yields better properties than CL. The tensile strength of CB-45 reaches 163.7 MPa for 10 mm/min feed rate. Whilst CL produces joint with tensile strength equal 120 MPa for equal parameters. Microstructure observation showed that CB-45 produces fine and homogenous appearance of MgO compared to CL. This phenomenon is caused by the pin of CB-45 joint which fully penetrates the nugget zone which is not found in CL design. This microstructure in turn promotes higher tensile strength of CB-45. |
| first_indexed | 2024-03-13T23:53:49Z |
| format | Conference or Workshop Item |
| id | oai:generic.eprints.org:274684 |
| institution | Universiti Gadjah Mada |
| language | English |
| last_indexed | 2024-03-13T23:53:49Z |
| publishDate | 2018 |
| record_format | dspace |
| spelling | oai:generic.eprints.org:2746842018-11-12T03:19:36Z https://repository.ugm.ac.id/274684/ Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding Setiawan, Widia Darmadi, Djarot B. Suprapto, Wahyono Soenoko, Rudy Manufacturing Processes and Technologies (excl. Textiles) The 10 mm thick Aluminum 6061 plates have been corner joined using varied design and those were 45ᴼ Corner Butt and Corner Lap Joints (CB-45 & CL). Friction tool was hardened EMS 45. True experimental method was used with independent parameters is feed rate which varied at 10 mm/min, 15 mm/min and 30 mm/min respectively. Other parameter such as rotating speed was kept constant. Experiment results show that, CB-45 yields better properties than CL. The tensile strength of CB-45 reaches 163.7 MPa for 10 mm/min feed rate. Whilst CL produces joint with tensile strength equal 120 MPa for equal parameters. Microstructure observation showed that CB-45 produces fine and homogenous appearance of MgO compared to CL. This phenomenon is caused by the pin of CB-45 joint which fully penetrates the nugget zone which is not found in CL design. This microstructure in turn promotes higher tensile strength of CB-45. 2018 Conference or Workshop Item PeerReviewed application/pdf en https://repository.ugm.ac.id/274684/1/matecconf_icet4sd2018_01106.pdf Setiawan, Widia and Darmadi, Djarot B. and Suprapto, Wahyono and Soenoko, Rudy (2018) Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding. In: ICET4SD 2017, Oktober 2017, Eastparc Hotel Yogyakarta. https://www.matec-conferences.org/articles/matecconf/abs/2018/13/matecconf_icet4sd2018_01106/matecconf_icet4sd2018_01106.html |
| spellingShingle | Manufacturing Processes and Technologies (excl. Textiles) Setiawan, Widia Darmadi, Djarot B. Suprapto, Wahyono Soenoko, Rudy Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding |
| title | Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding |
| title_full | Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding |
| title_fullStr | Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding |
| title_full_unstemmed | Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding |
| title_short | Comparison of Corner-Butt 45 (Cb-45) and Corner-Lap (Cl) joints in friction stir welding |
| title_sort | comparison of corner butt 45 cb 45 and corner lap cl joints in friction stir welding |
| topic | Manufacturing Processes and Technologies (excl. Textiles) |
| url | https://repository.ugm.ac.id/274684/1/matecconf_icet4sd2018_01106.pdf |
| work_keys_str_mv | AT setiawanwidia comparisonofcornerbutt45cb45andcornerlapcljointsinfrictionstirwelding AT darmadidjarotb comparisonofcornerbutt45cb45andcornerlapcljointsinfrictionstirwelding AT supraptowahyono comparisonofcornerbutt45cb45andcornerlapcljointsinfrictionstirwelding AT soenokorudy comparisonofcornerbutt45cb45andcornerlapcljointsinfrictionstirwelding |