UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser
Aluminum matrix composite (AMe) has been prepared from aluminum fine powder as a matrix and fly ash waste as reinforcement. In this research the amount of fly ash as much as 2.5,5, 7.5 and 10 wt% was added to the aluminum fine powder. The mixture was compacted using uniaxial with a pressure of 100 M...
| Main Author: | |
|---|---|
| Format: | Article |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2011
|
| Subjects: |
| _version_ | 1826033358504722432 |
|---|---|
| author | Perpustakaan UGM, i-lib |
| author_facet | Perpustakaan UGM, i-lib |
| author_sort | Perpustakaan UGM, i-lib |
| collection | UGM |
| description | Aluminum matrix composite (AMe) has been prepared from aluminum fine powder as a matrix and fly ash waste as reinforcement. In this research the amount of fly ash as much as 2.5,5, 7.5 and 10 wt% was added to the aluminum fine powder. The mixture was compacted using uniaxial with a pressure of 100 MPa and it was pressureless sintered in argon atmosphere at various temperature of 500°, 525°, 550°,575° and 600°C. Bending strength of AMC was determined using four point bending, hardness was tested using Vickers method, wear rate was tested using pin on disk method, porosity was tested using Archimedes method and the micro structure was observed using SEM. The result shows that fly ash can be used as reinforcement of AMC. The bending strength and Vickers hardness of AMC increase, wear rate and porosity of AMC decrease with increasing the fly ash content up to 7.5 wt%, while fly ash higher than 7.5 wt% causes a decrease. Porosity, bending strength, wear rate and hardness of AMC are 5.4%, 68.5 MPa, 0.0571 mg/(MPa.m) and 62.6 VHN, respectively. It shows that bending strength, hardness and wear resistance of AMC are higher than
pure aluminum. |
| first_indexed | 2024-03-13T19:09:37Z |
| format | Article |
| id | oai:generic.eprints.org:29117 |
| institution | Universiti Gadjah Mada |
| last_indexed | 2024-03-13T19:09:37Z |
| publishDate | 2011 |
| publisher | [Yogyakarta] : Universitas Gadjah Mada |
| record_format | dspace |
| spelling | oai:generic.eprints.org:291172014-06-18T00:23:47Z https://repository.ugm.ac.id/29117/ UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser Perpustakaan UGM, i-lib Jurnal i-lib UGM Aluminum matrix composite (AMe) has been prepared from aluminum fine powder as a matrix and fly ash waste as reinforcement. In this research the amount of fly ash as much as 2.5,5, 7.5 and 10 wt% was added to the aluminum fine powder. The mixture was compacted using uniaxial with a pressure of 100 MPa and it was pressureless sintered in argon atmosphere at various temperature of 500°, 525°, 550°,575° and 600°C. Bending strength of AMC was determined using four point bending, hardness was tested using Vickers method, wear rate was tested using pin on disk method, porosity was tested using Archimedes method and the micro structure was observed using SEM. The result shows that fly ash can be used as reinforcement of AMC. The bending strength and Vickers hardness of AMC increase, wear rate and porosity of AMC decrease with increasing the fly ash content up to 7.5 wt%, while fly ash higher than 7.5 wt% causes a decrease. Porosity, bending strength, wear rate and hardness of AMC are 5.4%, 68.5 MPa, 0.0571 mg/(MPa.m) and 62.6 VHN, respectively. It shows that bending strength, hardness and wear resistance of AMC are higher than pure aluminum. [Yogyakarta] : Universitas Gadjah Mada 2011 Article NonPeerReviewed Perpustakaan UGM, i-lib (2011) UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser. Jurnal i-lib UGM. http://i-lib.ugm.ac.id/jurnal/download.php?dataId=12180 |
| spellingShingle | Jurnal i-lib UGM Perpustakaan UGM, i-lib UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser |
| title | UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser |
| title_full | UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser |
| title_fullStr | UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser |
| title_full_unstemmed | UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser |
| title_short | UTILIZATION OF FLYASH WASTE AS REINFORCEMENT OF ALUMINUM MATRIX COMPOSITE PRODUCED USING POWDER METALLURGY (Pemanfaatan Limbah Abu Terbang sebagai Penguat Aluminium Metal Matrix Composite Dibuat dengan Cara Meta/urgi Ser |
| title_sort | utilization of flyash waste as reinforcement of aluminum matrix composite produced using powder metallurgy pemanfaatan limbah abu terbang sebagai penguat aluminium metal matrix composite dibuat dengan cara meta urgi ser |
| topic | Jurnal i-lib UGM |
| work_keys_str_mv | AT perpustakaanugmilib utilizationofflyashwasteasreinforcementofaluminummatrixcompositeproducedusingpowdermetallurgypemanfaatanlimbahabuterbangsebagaipenguataluminiummetalmatrixcompositedibuatdengancarametaurgiser |