PENGARUH INHIBITOR KALIUM KROMAT (K2CrO4) TERHADAP KOROSI DAN LAJU PERAMBATAN RETAK FATIK PADA ALUMINIUM PADUAN 2024-T3 DI LINGKUNGAN AIR LAUT

PENGARUH INHIBITOR KALIUM KROMAT (K2CrO4) TERHADAP KOROSI DAN LAJU PERAMBATAN RETAK FATIK PADA ALUMINIUM PADUAN 2024-T3 DI LINGKUNGAN AIR LAUT

Alluminium alloy 2024-T3 is widely used in manufacturing industries such as aircraft, outomotive and ship industries due to its light weight, high strength (up to 450 MPa) and relatively good resistance to corrosion. However, alluminium alloy is easily suffered from fatigue corrosion if it is applie...

Full description

Bibliographic Details
Main Authors:	, WARIS WIBOWO, , Mochammad Noer Ilman, S.T., M.Sc., Ph.D.
Format:	Thesis
Published:	[Yogyakarta] : Universitas Gadjah Mada 2011
Subjects:	ETD

Similar Items

PENGARUH PREHEAT TERHADAP LAJU PERAMBATAN RETAK FATIK SAMBUNGAN LAS TIG PADA PENGELASAN ALUMINIUM PADUAN 6061-T6
by: , Sirama, SST, et al.
Published: (2011)

Pengaruh artificial aging terhadap laju perambatan retak fatik AL 2024
by: , PURBOPUTRO, Pramuko Ilmu, et al.
Published: (2003)

Peningkatan ketahanan laju perambatan retak fatik las friction stir welding (FSW) pada pengelasan aluminium 2024-T3 dengan aplikasi transient thermal tensioning (TTT)
by: , PUJONO, et al.
Published: (2010)

Pengaruh Post-Weld Heat Treatment T6 Pada Laju Perambatan Retak Fatik Paduan Al 6013
by: Perpustakaan UGM, i-lib
Published: (2003)

Pengaruh post-weld heat treatment T6 terhadap laju perambatan retak fatik paduan AL 6013
by: , ISTANTO, Widia Lastana, et al.
Published: (2002)

Pengaruh stretching dan srtificial aging terhadap laju perambatan retak fatik AL 2024
by: , SUGITO, Bibit, et al.
Published: (2003)

Pengaruh pembebanan multi overload terhadap perilaku perambatan retak fatik aluminium paduan AL 2024-T3
by: , PURWADIANTO, Doddy, et al.
Published: (2002)

Pengaruh shot peening terhadap laju perambatan retak fatik pada paduan Al 2024-T3 dan Al 2524-T3 yang distretching
by: , MUJIYONO, et al.
Published: (2001)

PENGARUHSHOTPEENINGTERHADAP SIFAT MEKANIS DAN LAJU PERAMBATAN RETAK FATIK SAMBUNGAN FRICTION STIR WELDINGPADA ALUMINIUM SERI 5083
by: , WARTONO, et al.
Published: (2013)

Laju perambatan retak fatik Wheel Hub Al 2014-T61
by: , HESTIAWAN, Hendri, et al.
Published: (2004)

Pengaruh luas penampang tambalan komposit terhadap laju perambatan retak aluminium paduan 2024-T3
by: , BALFAS, Muhammad, et al.
Published: (2000)

Pengaruh suhu preheat terhadap perilaku laju perambatan retak fatik sambungan friction stir welding (FSW) pada aluminium 6061-T6
by: , HENDRARTININGSIH, Sckolastika Ninien Henny Sri Rochani, et al.
Published: (2010)

Pengaruh putaran dan kecepatan tool terhadap perilaku laju perambatan retak fatik sambungan las FSW tak sejenis antara Al 2024-T3 dengan Al 1100
by: , HARIYANTO, et al.
Published: (2009)

PENGARUH RAPAT ARUS DAN WAKTU ANODIZING TERHADAP LAJU KOROSI DAN KEAUSAN PADA ALUMINIUM PADUAN 2024-T3
by: , FAJAR NUGROHO, et al.
Published: (2011)

Pengaruh Pengendapan Kromium Karbida Terhadap Karakteristik Laju Perambatan Retak Fatik Aisi 304
by: Perpustakaan UGM, i-lib
Published: (2004)

Pengaruh kecepatan Flame Heating terhadap laju perambatan retak fatik las busur rendam pada pengelasan baja ASTM A-572 Grade 50
by: , ISMAIL, Rifky, et al.
Published: (2007)

Analisis perilaku laju perambatan retak fatik berdasarkan beban lebih tunggal pada al-2024-T3 produk chemical milling
by: , JAMAL, Abdul Muzakkar, et al.
Published: (1998)

Pengaruh basicity index fliks terhadap struktur mikro ketangguhan dan laju rambatan retak fatik sambungan las busur rendam baja paduan rendah HSLA
by: , PURWANINGRUM, Yustiasih, et al.
Published: (2005)

Aplikasi perlakuan transient thermal tensioning (TTT) guna peningkatan ketangguhan dan ketahanan laju perambatan retak fatik sambungan las GMAW baja AISI 1018
by: , WIJOYO, et al.
Published: (2009)

Mekanisme korosi dan perilaku perambatan retak fatik sambungan las FSW (friction stir welding) tak sejenis antara Al 2024-T3 dan Al 1100 dalam media korosif dengan variasi konsentrasi NaCl
by: , KUSDIYARTO, Prihatno, et al.
Published: (2009)

Pengaruh suhu pemanasan mula pengelasan baja karbon rendah terhadap laju perambatan retak fatik
by: , DARMADI, Djarot B, et al.
Published: (2003)

Pengaruh Perlakuan Panas Terhadap Laju Perambatan Retak Fatik Baja Tahan Karat Aisi 304
by: Perpustakaan UGM, i-lib
Published: (1997)

Perilaku Laju Perambatan Retak Fatik Pada Hasil Pengelasan Tig Al 6061 â�� T4
by: Perpustakaan UGM, i-lib
Published: (2002)

PENGARUH PREHEAT DAN STATIC â�� TRANSIENT THERMAL TENSIONING TERHADAP SIFAT MEKANIK DAN LAJU PERAMBATAN RETAK FATIK PADA SAMBUNGAN LAS TIG Al 6061-T6
by: , YUNAIDI, et al.
Published: (2012)

Pengaruh perlakuan post-weld shot peening terhadap laju perambatan retak fatik AL 6061-T4
by: , NAFRIZAL, et al.
Published: (2001)

Pengaruh arah pelengkungan terhadap laju perambatan retak fatik bahan ketel SA 285 Gr.C
by: , SUTRISNA, et al.
Published: (2003)

Pengaruh Beban Lebih Majemuk Terhadap Laju Perambatan Retak Fatik Baja Tahan Karat Aisi 304
by: Perpustakaan UGM, i-lib
Published: (2000)

Pengaruh jenis filler pada proses pengelasan TIG terhadap perilaku perambatan retak fatik paduan AL 6061-T4
by: , SULARDJAKA, et al.
Published: (2001)

Pengaruh Heat input pada pengelasan Submerged ARC Welding (SAW) terhadap ketangguhan dan laju perambatan retak fatik baja SM 490
by: , SUHARNO, et al.
Published: (2004)

Pengaruh temperatur flame stess relieving terhadap laju perambatan retak fatik sambungan las busur rendam pada baja ASTM A572 Grade 50 di lingkungan air laut
by: , WIJAYANTO, Jarot, et al.
Published: (2008)

Percabangan retak sebagai bentuk penahanan perambatan retak fatik pada bahan perunggu keras
by: Perpustakaan UGM, i-lib
Published: (2001)

Studi perambatan retak fatik pada pipa baja karbon rendah
by: , HUTABARAT, Udur 1 Januari, et al.
Published: (2005)

Pengaruh jarak Flame Heating dari garis las terhadap tegangan sisa dan laju perambatan retak fatik las busur terendam pada pengelasan baja ASTM A572 Grade 50
by: , ISWAHYUDI, Sigit, et al.
Published: (2007)

Pengaruh perentangan dan chemical milling terhadap sifat mekanis dan laju perambatan retak pada paduan aluminium
by: , ARIYANO, et al.
Published: (2000)

Pengaruh pengerjaan dingin terhadap perilaku perambatan retak aluminium paduan
by: , SUMIRAT, Uum, et al.
Published: (2000)

Pengembangan Metode Stress Relief Berdasarkan Transient Thermal Tension Untuk Mengurangi Tegangan Sisa dan Meningkatkan Ketahanan Terhadap Laju Perambatan Retak Fatik Sambungan Las FSW Pada Pelat Aluminium dan Potensinya sebagai Bahan Gerbong Kereta Api
by: , Mochammad Noer llman
Published: (2009)

Pengaruh Perlakuan Panas T-82 Pada Al 6013 Yang Telah Mengalami Proses Pengelasan Terhadap Laju Perambatan Retak Fatik
by: Perpustakaan UGM, i-lib
Published: (2004)

Pengaruh perlakuan panas T82 pada AL 6013 yang telah mengalami proses pengelasan terhadap laju perambatan retak fatik
by: , HARYADI, Gunawan Dwi, et al.
Published: (2002)

Pengaruh shot peening terhadap laju perambatan retak fatik pada produk chemical milling Al 2024-T3 dan Al 2524-T3 yang telah di stretching
by: , YOVIAL, et al.
Published: (2000)

Pengaruh Jenis Filler Pada Pengelasan Tig Transversal Butt Joint Terhadap Perilaku Perambatan Retak Fatik Pada Pengelasan Paduan AL 6061-T4
by: Perpustakaan UGM, i-lib
Published: (2003)