STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS
The issue that material must high-perfomance in strengthness, stiffness, toughness, lighter and cheaper. The properties of polymeric thermoset of unsaturated polyester were brittle and crack sensitive can be repaired by added fiber glass and clay in number of amount.The aim of this study was to dete...
| Main Authors: | , |
|---|---|
| Format: | Thesis |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2012
|
| Subjects: |
| _version_ | 1797032156964323328 |
|---|---|
| author | , HUSAINI, ST. , Bapak Dr. Kusmono, ST., MT |
| author_facet | , HUSAINI, ST. , Bapak Dr. Kusmono, ST., MT |
| author_sort | , HUSAINI, ST. |
| collection | UGM |
| description | The issue that material must high-perfomance in strengthness, stiffness,
toughness, lighter and cheaper. The properties of polymeric thermoset of
unsaturated polyester were brittle and crack sensitive can be repaired by added
fiber glass and clay in number of amount.The aim of this study was to determine
the effect of the addition of clay on the tensile strength, bending strength, bending
modulus of elasticity, impact strength and fracture toughness of the composite
unsaturated polyester / glass fiber.
Handy lay-up method was used for the preparation of the unsaturated
polyester/clay/glass fiber hybrid composite. The materials used in this study was
unsaturated polyester resin, clay, glass fiber and methyl ethyl ketone peroxide
catalist into unsaturated polyester then clay using variations of 0, 2, 4 and 6 %wt
were mixed stirred mechanically 800 rpm for 120 minutes at 60
o
C. The mixture
were cooled for 10 minutes, then added of 1 %wt catalist, stirred for 2 minutes
and put in a vacuum oven for 2 minutes. Hybrid composite composed of
unsaturated polyester / clay and 4 layers glass fiber by size 190 x 220 mm
2
. Firstly
matrix of unsaturated polyester / clay was poured into a metal mold, then first ply
of glass fibers layed on the matrix and compressed using rollers. The matrix was
poured over the first ply of glass fiber and then placed a second ply of glass fiber.
This process was repeated up to 4 plies glass fiber. After settling for 24 hours at
room temperature, unsaturated polyester hybrid composite clay / glass fiber ware
heated at a temperature of 80 °C for 3 hours. Furthermore, the spesimen was made
by a �scroll saw� machine.
Results showed that the highest value tensile strength, bending strength and
bending modulus of elasticity were obtained in the hybrid composite unsaturated
polyester / clay / glass fiber using 2 %wt of clay content. The pencentage increase
by 12.83% tensile strength, 21.12% for bending strength, and 11.15% for bending
modulus of elasticity. But impact strength and fracture toughness of the hybrid
composite unsaturated polyester / clay / glass fiber was achieved on clay 4 %wt for
the impact strength increas by 26,19% and by 14.43% fracture toughness. |
| first_indexed | 2024-03-13T22:34:11Z |
| format | Thesis |
| id | oai:generic.eprints.org:97878 |
| institution | Universiti Gadjah Mada |
| last_indexed | 2024-03-13T22:34:11Z |
| publishDate | 2012 |
| publisher | [Yogyakarta] : Universitas Gadjah Mada |
| record_format | dspace |
| spelling | oai:generic.eprints.org:978782016-03-04T08:46:52Z https://repository.ugm.ac.id/97878/ STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS , HUSAINI, ST. , Bapak Dr. Kusmono, ST., MT ETD The issue that material must high-perfomance in strengthness, stiffness, toughness, lighter and cheaper. The properties of polymeric thermoset of unsaturated polyester were brittle and crack sensitive can be repaired by added fiber glass and clay in number of amount.The aim of this study was to determine the effect of the addition of clay on the tensile strength, bending strength, bending modulus of elasticity, impact strength and fracture toughness of the composite unsaturated polyester / glass fiber. Handy lay-up method was used for the preparation of the unsaturated polyester/clay/glass fiber hybrid composite. The materials used in this study was unsaturated polyester resin, clay, glass fiber and methyl ethyl ketone peroxide catalist into unsaturated polyester then clay using variations of 0, 2, 4 and 6 %wt were mixed stirred mechanically 800 rpm for 120 minutes at 60 o C. The mixture were cooled for 10 minutes, then added of 1 %wt catalist, stirred for 2 minutes and put in a vacuum oven for 2 minutes. Hybrid composite composed of unsaturated polyester / clay and 4 layers glass fiber by size 190 x 220 mm 2 . Firstly matrix of unsaturated polyester / clay was poured into a metal mold, then first ply of glass fibers layed on the matrix and compressed using rollers. The matrix was poured over the first ply of glass fiber and then placed a second ply of glass fiber. This process was repeated up to 4 plies glass fiber. After settling for 24 hours at room temperature, unsaturated polyester hybrid composite clay / glass fiber ware heated at a temperature of 80 °C for 3 hours. Furthermore, the spesimen was made by a �scroll saw� machine. Results showed that the highest value tensile strength, bending strength and bending modulus of elasticity were obtained in the hybrid composite unsaturated polyester / clay / glass fiber using 2 %wt of clay content. The pencentage increase by 12.83% tensile strength, 21.12% for bending strength, and 11.15% for bending modulus of elasticity. But impact strength and fracture toughness of the hybrid composite unsaturated polyester / clay / glass fiber was achieved on clay 4 %wt for the impact strength increas by 26,19% and by 14.43% fracture toughness. [Yogyakarta] : Universitas Gadjah Mada 2012 Thesis NonPeerReviewed , HUSAINI, ST. and , Bapak Dr. Kusmono, ST., MT (2012) STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS. UNSPECIFIED thesis, UNSPECIFIED. http://etd.ugm.ac.id/index.php?mod=penelitian_detail&sub=PenelitianDetail&act=view&typ=html&buku_id=54544 |
| spellingShingle | ETD , HUSAINI, ST. , Bapak Dr. Kusmono, ST., MT STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS |
| title | STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS |
| title_full | STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS |
| title_fullStr | STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS |
| title_full_unstemmed | STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS |
| title_short | STUDI SIFAT MEKANIK KOMPOSIT HIBRID UNSATURATED POLYESTER/CLAY/SERAT GELAS |
| title_sort | studi sifat mekanik komposit hibrid unsaturated polyester clay serat gelas |
| topic | ETD |
| work_keys_str_mv | AT husainist studisifatmekanikkomposithibridunsaturatedpolyesterclayseratgelas AT bapakdrkusmonostmt studisifatmekanikkomposithibridunsaturatedpolyesterclayseratgelas |