PENGARUH JENIS BAHAN BONDING SELF ETCH TERHADAP KEBOCORAN MIKRO TUMPATAN RESIN KOMPOSIT SILORANE KAVITAS KELAS I
The aim of this study was to know the influence of bonding system self etch to microleakage of silorane composit resin class I direct restoration. Eighteen caries free maxillary premolar teeth divided specimen were devided evenly into three experimental group of six each cavity in the occlusal area...
| Main Authors: | , |
|---|---|
| Format: | Thesis |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2012
|
| Subjects: |
| Summary: | The aim of this study was to know the influence of bonding system self
etch to microleakage of silorane composit resin class I direct restoration.
Eighteen caries free maxillary premolar teeth divided specimen were
devided evenly into three experimental group of six each cavity in the occlusal
area were prepared with diamond bur. Group I was bonded with silorane
system adhesive, group II was bonded with adper prompt L-pop bonding
system and group III was bonded with adper easy one bonding system. The
silorane composite resin was placed incrementally and polished with soflex
disc. Specimen store in artificial saliva for 24 hours at 37 0C the teeth were
thermocycled 40 C and 600C each of 1 minute and were immersed in 2%
methylene blue for 24 hours. All teeth were sectioned in sagital direction and
the depth of penetration was scored (0-3). Data obtained were analyzed using
Kruskal Walls test at < 0,05 significancee level and 95%.
Silorane confidence level there was no significant different
microleakage silorane composite resin of class I direct restorations. The result
showed no different microleakage of class I direct restorations silorane
composite resin with using bonding self etch material |
|---|