Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.]
An experimental investigation was performed to evaluate the properties of cement-bonded particleboard made from Sesendok wood. The target board density was set at a standard 1200 kg m". The effect offarticle size, wood to cement ratio and the addition ofsodium silicate and aluminium silicate...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Research Management Institute (RMI)
2010
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/12936/2/AJ_JAMALUDIN%20KASIM%20SRJ%2010.pdf |
| _version_ | 1796899811145809920 |
|---|---|
| author | Kasim, Jamaludin |
| author_facet | Kasim, Jamaludin |
| author_sort | Kasim, Jamaludin |
| collection | UITM |
| description | An experimental investigation was performed to evaluate the properties of
cement-bonded particleboard made from Sesendok wood. The target board
density was set at a standard 1200 kg m". The effect offarticle size, wood to
cement ratio and the addition ofsodium silicate and aluminium silicate on the
wood cement board properties has been evaluated. A change ofparticle size
from 1.0 mm to 2.0 mm has a significant effect on the mechanical properties,
however the physical properties deteriorate. Increasing the wood to cement
ratio from 1:2.25 to 1:3 decreases the modulus ofrupture (MOR) by 11% and
the addition ofsodium silicate improves valuesfurther by about 28% compared
to the addition ofaluminum silicate. The modulus ofelasticity (MOE) in general
increases with increasing cement content, but is not significantly affected by
the addition ofsodium silicate or aluminium silicate, although the addition of
their mixture (sodium silicate andaluminium silicate) consistentlyyields greater
MOE values. Water absorption and thickness swelling is significantly affected
by the inclusion ofadditives and better values are attained using higher wood
to cement ratios. |
| first_indexed | 2024-03-06T01:26:25Z |
| format | Article |
| id | oai:ir.uitm.edu.my:12936 |
| institution | Universiti Teknologi MARA |
| language | English |
| last_indexed | 2024-03-06T01:26:25Z |
| publishDate | 2010 |
| publisher | Research Management Institute (RMI) |
| record_format | dspace |
| spelling | oai:ir.uitm.edu.my:129362019-11-15T02:17:11Z https://ir.uitm.edu.my/id/eprint/12936/ Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.] srj Kasim, Jamaludin Particle size determination Engineered wood. Fiberboard, particle board, etc. An experimental investigation was performed to evaluate the properties of cement-bonded particleboard made from Sesendok wood. The target board density was set at a standard 1200 kg m". The effect offarticle size, wood to cement ratio and the addition ofsodium silicate and aluminium silicate on the wood cement board properties has been evaluated. A change ofparticle size from 1.0 mm to 2.0 mm has a significant effect on the mechanical properties, however the physical properties deteriorate. Increasing the wood to cement ratio from 1:2.25 to 1:3 decreases the modulus ofrupture (MOR) by 11% and the addition ofsodium silicate improves valuesfurther by about 28% compared to the addition ofaluminum silicate. The modulus ofelasticity (MOE) in general increases with increasing cement content, but is not significantly affected by the addition ofsodium silicate or aluminium silicate, although the addition of their mixture (sodium silicate andaluminium silicate) consistentlyyields greater MOE values. Water absorption and thickness swelling is significantly affected by the inclusion ofadditives and better values are attained using higher wood to cement ratios. Research Management Institute (RMI) 2010 Article PeerReviewed text en https://ir.uitm.edu.my/id/eprint/12936/2/AJ_JAMALUDIN%20KASIM%20SRJ%2010.pdf Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.]. (2010) Scientific Research Journal <https://ir.uitm.edu.my/view/publication/Scientific_Research_Journal/>, 7 (2). pp. 57-65. ISSN 1675-7009 https://srj.uitm.edu.my/ |
| spellingShingle | Particle size determination Engineered wood. Fiberboard, particle board, etc. Kasim, Jamaludin Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.] |
| title | Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.] |
| title_full | Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.] |
| title_fullStr | Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.] |
| title_full_unstemmed | Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.] |
| title_short | Effects of particle sizes, wood to cement ratio and chemical additives on the properties of sesendok (Endospermum Diadenum) cement-bonded particleboard / Jamaludin Kasim ... [et al.] |
| title_sort | effects of particle sizes wood to cement ratio and chemical additives on the properties of sesendok endospermum diadenum cement bonded particleboard jamaludin kasim et al |
| topic | Particle size determination Engineered wood. Fiberboard, particle board, etc. |
| url | https://ir.uitm.edu.my/id/eprint/12936/2/AJ_JAMALUDIN%20KASIM%20SRJ%2010.pdf |
| work_keys_str_mv | AT kasimjamaludin effectsofparticlesizeswoodtocementratioandchemicaladditivesonthepropertiesofsesendokendospermumdiadenumcementbondedparticleboardjamaludinkasimetal |