Properties of oriented strand board (OSB) from acacia mangium and rubberwood / Zainab Haris
This study used Acacia mangium and rubberwood species as the raw materials in manufacture of oriented strand board (OSB). The objectives of this study were to determine the physical and mechanical properties of OSB using Acacia mangium and rubberwood, and effect of different board densities (600...
| Main Author: | |
|---|---|
| Format: | Student Project |
| Language: | English |
| Published: |
Faculty of Applied Sciences
2015
|
| Subjects: | |
| Online Access: | https://ir.uitm.edu.my/id/eprint/19990/1/PPb_ZAINAB%20HARIS%20AS%20C%2015_5.pdf.PDF |
| _version_ | 1796901111295115264 |
|---|---|
| author | Haris, Zainab |
| author_facet | Haris, Zainab |
| author_sort | Haris, Zainab |
| collection | UITM |
| description | This study used Acacia mangium and rubberwood species as the raw
materials in manufacture of oriented strand board (OSB). The objectives of
this study were to determine the physical and mechanical properties of OSB
using Acacia mangium and rubberwood, and effect of different board densities
(600 kg/m3 and 700 kg/m3
) and wood species ratio on properties. In this study,
phenol formaldehyde (PF) was use as a binder and it was fixed at 9%.
Oriented strand board was assessed for the mechanical properties (bending
and internal bonding) and physical properties (thickness swelling) according to
European Standard (EN 300: 1993). Mechanical properties revealed the
highest MOR (34.18 MPa) and MOE (6 835.78 MPa) with higher board density
of 700 kg/m3 from 100% Acacia mangium. However, the highest results for IB
value was 1.32 MPa from L4 layer with lower board density of 600kg/m3
.
Furthermore, for the physical properties with density board of 600kglm3 with
100% Acacia mangium strands point the lowest TS value with 27.24%. The
results revealed that board density show significant effect on mechanical
properties except for lB. However, TS values were not significant. |
| first_indexed | 2024-03-06T01:45:15Z |
| format | Student Project |
| id | oai:ir.uitm.edu.my:19990 |
| institution | Universiti Teknologi MARA |
| language | English |
| last_indexed | 2024-03-06T01:45:15Z |
| publishDate | 2015 |
| publisher | Faculty of Applied Sciences |
| record_format | dspace |
| spelling | oai:ir.uitm.edu.my:199902019-05-15T05:07:19Z https://ir.uitm.edu.my/id/eprint/19990/ Properties of oriented strand board (OSB) from acacia mangium and rubberwood / Zainab Haris Haris, Zainab Agroforestry Wood technology. Lumber This study used Acacia mangium and rubberwood species as the raw materials in manufacture of oriented strand board (OSB). The objectives of this study were to determine the physical and mechanical properties of OSB using Acacia mangium and rubberwood, and effect of different board densities (600 kg/m3 and 700 kg/m3 ) and wood species ratio on properties. In this study, phenol formaldehyde (PF) was use as a binder and it was fixed at 9%. Oriented strand board was assessed for the mechanical properties (bending and internal bonding) and physical properties (thickness swelling) according to European Standard (EN 300: 1993). Mechanical properties revealed the highest MOR (34.18 MPa) and MOE (6 835.78 MPa) with higher board density of 700 kg/m3 from 100% Acacia mangium. However, the highest results for IB value was 1.32 MPa from L4 layer with lower board density of 600kg/m3 . Furthermore, for the physical properties with density board of 600kglm3 with 100% Acacia mangium strands point the lowest TS value with 27.24%. The results revealed that board density show significant effect on mechanical properties except for lB. However, TS values were not significant. Faculty of Applied Sciences 2015 Student Project NonPeerReviewed text en https://ir.uitm.edu.my/id/eprint/19990/1/PPb_ZAINAB%20HARIS%20AS%20C%2015_5.pdf.PDF Properties of oriented strand board (OSB) from acacia mangium and rubberwood / Zainab Haris. (2015) [Student Project] <http://terminalib.uitm.edu.my/19990.pdf> (Unpublished) |
| spellingShingle | Agroforestry Wood technology. Lumber Haris, Zainab Properties of oriented strand board (OSB) from acacia mangium and rubberwood / Zainab Haris |
| title | Properties of oriented strand board (OSB) from
acacia mangium and rubberwood / Zainab Haris |
| title_full | Properties of oriented strand board (OSB) from
acacia mangium and rubberwood / Zainab Haris |
| title_fullStr | Properties of oriented strand board (OSB) from
acacia mangium and rubberwood / Zainab Haris |
| title_full_unstemmed | Properties of oriented strand board (OSB) from
acacia mangium and rubberwood / Zainab Haris |
| title_short | Properties of oriented strand board (OSB) from
acacia mangium and rubberwood / Zainab Haris |
| title_sort | properties of oriented strand board osb from acacia mangium and rubberwood zainab haris |
| topic | Agroforestry Wood technology. Lumber |
| url | https://ir.uitm.edu.my/id/eprint/19990/1/PPb_ZAINAB%20HARIS%20AS%20C%2015_5.pdf.PDF |
| work_keys_str_mv | AT hariszainab propertiesoforientedstrandboardosbfromacaciamangiumandrubberwoodzainabharis |