Luminescence properties of nanocrystalline Y2O3:Eu
Y2O2:Eu nanocrystals in the size range 70-100 nm were fabricated. The crystals show a photoluminescence efficiency 10-20% higher than commercial bulk material. It was found that under electron excitation, the nanocrystalline material is 50% more efficient than the bulk at 1 kV accelerating voltage.
| Main Authors: | , , , |
|---|---|
| Format: | Journal article |
| Language: | English |
| Published: |
2001
|
| Summary: | Y2O2:Eu nanocrystals in the size range 70-100 nm were fabricated. The crystals show a photoluminescence efficiency 10-20% higher than commercial bulk material. It was found that under electron excitation, the nanocrystalline material is 50% more efficient than the bulk at 1 kV accelerating voltage. |
|---|