Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB

Preparation of TEM specimens containing stress corrosion cracks in austenitic alloys using FIB

Bibliographische Detailangaben
Hauptverfasser:	Lozano-Perez, S, Huang, Y, Langford, R, Titchmarsh, J
Format:	Conference item
Veröffentlicht:	2001

Ähnliche Einträge

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
von: Lozano-Perez, S, et al.
Veröffentlicht: (2003)

TEM investigations of intergranular stress corrosion cracking in austenitic alloys in PWR environmental conditions
von: Lozano-Perez, S, et al.
Veröffentlicht: (2003)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis
von: Lozano-Perez, S
Veröffentlicht: (2008)

A guide on FIB preparation of samples containing stress corrosion crack tips for TEM and atom-probe analysis.
von: Lozano-Perez, S
Veröffentlicht: (2008)

TEM characterization of stress corrosion cracks in 304SS
von: Lozano-Perez, S, et al.
Veröffentlicht: (2004)

TEM characterization of stress corrosion cracks in 304SS
von: Lozano-Perez, S, et al.
Veröffentlicht: (2004)

Preparation of transmission electron microscopy cross-section specimens of crack tips using focused ion beam milling
von: Huang, Y, et al.
Veröffentlicht: (2002)

Preparation of transmission electron microscopy cross-section specimens of crack tips using focused ion beam milling.
von: Huang, Y, et al.
Veröffentlicht: (2002)

3D visualisation of crack distributions in oxidised zirconium alloys by FIB-slicing
von: Grovenor, C, et al.
Veröffentlicht: (2012)

Preparation of site specific transmission electron microscopy plan-view specimens using a focused ion beam system
von: Langford, R, et al.
Veröffentlicht: (2001)

Investigation of chloride stress corrosion cracking in austenitic stainless steel
von: Mohamad Khairuazlan, Kamaruzaman
Veröffentlicht: (2013)

Determination of the Fe content of embedded Cu-rich particles in ferritic alloys using energy-filtered TEM
von: Lozano-Perez, S, et al.
Veröffentlicht: (2006)

Determination of the Fe content of embedded Cu-rich particles in ferritic alloys using energy-filtered TEM.
von: Lozano-Perez, S, et al.
Veröffentlicht: (2006)

TEM crack tip investigations of SCC
von: Lozano-Perez, S, et al.
Veröffentlicht: (2002)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
von: Huang, Y, et al.
Veröffentlicht: (2001)

Preparation of site specific transmission electron microscopy plan-view specimens using a focused ion beam system
von: Langford, R, et al.
Veröffentlicht: (2001)

In situ cryo-FIB/SEM Specimen Preparation Using the Waffle Method
von: Oleg Klykov, et al.
Veröffentlicht: (2022-11-01)

Influence of milling on the development of stress corrosion cracks in austenitic stainless steel
von: Lyon, K, et al.
Veröffentlicht: (2014)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
von: Kovac, J, et al.
Veröffentlicht: (2012)

Mechanical criterion for nucleation of intergranular stress corrosion cracking in austenitic stainless steel
von: Tomoyuki Fujii, et al.
Veröffentlicht: (2021-09-01)

Novel characterization of stress corrosion cracks
von: Lozano-Perez, S
Veröffentlicht: (2008)

Novel characterization of stress corrosion cracks
von: Lozano-Perez, S
Veröffentlicht: (2008)

High temperature and stress corrosion cracking of 310S austenitic stainless steel in wet chloride corrosive environment
von: T. Pornpibunsompop, et al.
Veröffentlicht: (2018-01-01)

Cryogenic large volume 3D and TEM sample preparation with multiple ion species plasma FIB
von: Wu Min, et al.
Veröffentlicht: (2024-01-01)

FIB-SEM/microtoming prepared Cross Section of a Stone Wool Fiber enabling (S)TEM investigation
von: Rasmussen Krestine Hofstedt, et al.
Veröffentlicht: (2024-01-01)

FIB and Wedge Polishing Sample Preparation for TEM Analysis of Sol-Gel Derived Perovskite Thin Films
von: Jorge Sanz-Mateo, et al.
Veröffentlicht: (2022-07-01)

Stress corrosion cracking of aluminium alloys /
von: 333484 Jainal Bonandar
Veröffentlicht: (1986)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
von: Marrow, T, et al.
Veröffentlicht: (2006)

Effects of Micro-Shot Peening on the Stress Corrosion Cracking of Austenitic Stainless Steel Welds
von: Chia-Ying Kang, et al.
Veröffentlicht: (2022-12-01)

Subsurface damage analysis by TEM and 3D FIB crack mapping in alumina and alumina/5vol.%SiC nanocomposites
von: Wu, H, et al.
Veröffentlicht: (2003)

Combination of focused ion beam (FIB) and microtome by ultrathin slice preparation for transmission electron microscopy (TEM) observation
von: Yuchen Xu, et al.
Veröffentlicht: (2018-09-01)

Understanding stress corrosion cracking with electron tomography
von: Lozano-Perez, S, et al.
Veröffentlicht: (2008)

Atmospheric-Induced Stress Corrosion Cracking of austenitic stainless steels under limited chloride supply
von: Cook, A, et al.
Veröffentlicht: (2011)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
von: Rahimi, S, et al.
Veröffentlicht: (2019)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
von: Babout, L, et al.
Veröffentlicht: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
von: Babout, L, et al.
Veröffentlicht: (2006)

Nanoindentation Investigation of Chloride-Induced Stress Corrosion Crack Propagation in an Austenitic Stainless Steel Weld
von: Haozheng J. Qu, et al.
Veröffentlicht: (2022-07-01)

Austenitic Stainless-Steel Reinforcement for Seawater Sea Sand Concrete: Investigation of Stress Corrosion Cracking
von: Xiang Yu, et al.
Veröffentlicht: (2021-03-01)

Effects of Multi-Pass Turning on Stress Corrosion Cracking of AISI 304 Austenitic Stainless Steel
von: Yansong Zhang, et al.
Veröffentlicht: (2022-10-01)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
von: S. Rahimi, et al.
Veröffentlicht: (2020-02-01)