Effect of current density on the solid electrolyte interphase formation at the lithium∣Li6PS5Cl interface
<p>Understanding the chemical composition and morphological evolution of the solid electrolyte interphase (SEI) formed at the interface between the lithium metal electrode and an inorganic solid-state electrolyte is crucial for developing reliable all-solid-state lithium batteries. To better u...
| Main Authors: | , , , , , |
|---|---|
| 格式: | Journal article |
| 语言: | English |
| 出版: |
Springer Nature
2022
|
| 总结: | <p>Understanding the chemical composition and morphological evolution of the solid electrolyte interphase (SEI) formed at the interface between the lithium metal electrode and an inorganic solid-state electrolyte is crucial for developing reliable all-solid-state lithium batteries. To better understand the interaction between these cell components, we carry out X-ray photoemission spectroscopy (XPS) measurements during lithium plating on the surface of a Li<sub>6</sub>PS<sub>5</sub>Cl solid-state electrolyte pellet using an electron beam. The analyses of the XPS data highlight the role of Li plating current density on the evolution of a uniform and ionically conductive (i.e., Li<sub>3</sub>P-rich) SEI capable of decreasing the electrode∣solid electrolyte interfacial resistance. The XPS findings are validated via electrochemical impedance spectrsocopy measurements of all-solid-state lithium-based cells.</p> |
|---|