| Summary: | We study the magnetic structure of the 'stuffed' (Tb-rich) pyrochlore iridate Tb2+x Ir2-x O7-y (x ∼ 0.18), using resonant elastic x-ray scattering (REXS). In order to disentangle contributions from Tb and Ir magnetic sublattices, experiments were performed at the Ir L 3 and Tb M 5 edges, which provide selective sensitivity to Ir 5d and Tb 4f magnetic moments, respectively. At the Ir L 3 edge, we found the onset of long-range [Formula: see text] magnetic order below [Formula: see text] K, consistent with the expected signal of all-in all-out (AIAO) magnetic order. Using a single-ion model to calculate REXS cross-sections, we estimate an ordered magnetic moment of [Formula: see text] at 5 K. At the Tb M 5 edge, long-range [Formula: see text] magnetic order appeared below ∼[Formula: see text] K, also consistent with an AIAO magnetic structure on the Tb site. Additional insight into the magnetism of the Tb sublattice is gleaned from measurements at the M 5 edge in applied magnetic fields up to 6 T, which is found to completely suppress the Tb AIAO magnetic order. In zero applied field, the observed gradual onset of the Tb sublattice magnetisation with temperature suggests that it is induced by the magnetic order on the Ir site. The persistence of AIAO magnetic order, despite the greatly reduced ordering temperature and moment size compared to stoichiometric Tb2Ir2O7, for which [Formula: see text] K and [Formula: see text], indicates that stuffing could be a viable means of tuning the strength of electronic correlations, thereby potentially offering a new strategy to achieve topologically non-trivial band crossings in pyrochlore iridates.
|
|---|