Rates of intergranular environment assisted cracking in three-dimensional model microstructures

Rates of intergranular environment assisted cracking in three-dimensional model microstructures

Microstructure can have a significant effect on the materials' resistance to intergranular environment assisted cracking. Certain grain boundaries are susceptible to degradation by stress corrosion while others have high resistance, and it is recognised that increasing the fraction of resistant...

书目详细资料
Main Authors:	Jivkov, A, Marrow, T
格式:	Journal article
语言:	English
出版:	2007

相似书籍

Modelling intergranular stress corrosion cracking in simulated three-dimensional microstructures
由: Jivkov, A, et al.
出版: (2007)

A three-dimensional computational model for intergranular cracking
由: Jivkov, A, et al.
出版: (2006)

The roles of microstructure and mechanics in intergranular stress corrosion cracking
由: Jivkov, A, et al.
出版: (2005)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
由: Jivkov, A, et al.
出版: (2008)

Mesoscale mechanical model for intergranular stress corrosion cracking and implications for microstructure engineering
由: Jivkov, A, et al.
出版: (2008)

A two-dimensional mesoscale model for intergranular stress corrosion crack propagation
由: Jivkov, A, et al.
出版: (2006)

Three dimensional observations and modelling of intergranular stress corrosion cracking in austenitic stainless steel
由: Marrow, T, et al.
出版: (2006)

Intergranular stress corrosion crack propagation in sensitised austenitic stainless steel (microstructure modelling and experimental observation)
由: Marrow, T, et al.
出版: (2006)

Intergranular crack nucleation in polycrystalline alumina
由: Aswad, M, et al.
出版: (2010)

Intergranular crack nucleation in polycrystalline alumina
由: Aswad, M, et al.
出版: (2010)

Intergranular crack nuclei in polycrystalline alumina
由: Aswad, M, et al.
出版: (2012)

Intergranular crack nuclei in polycrystalline alumina
由: Aswad, M, et al.
出版: (2012)

IN-SITU OBSERVATIONS OF INTERGRANULAR STRESS CORROSION CRACKING
由: Duff, J, et al.
出版: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
由: Zhang, Y, et al.
出版: (2009)

3D modelling of intergranular stress corrosion cracking (IGSCC)
由: Zhang, Y, et al.
出版: (2009)

In-situ observation and modelling of intergranular cracking in polycrystalline alumina
由: Marrow, T, et al.
出版: (2011)

Influence of microstructure and stress on short intergranular stress corrosion crack growth in austenitic stainless steel type 304
由: Rahimi, S, et al.
出版: (2008)

New techniques for intergranular stress corrosion crack observation
由: Marrow, T, et al.
出版: (2008)

Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
由: Kovac, J, et al.
出版: (2012)

Grain boundary engineering for crack bridging: A new model for intergranular stress corrosion crack (IGSCC) propagation
由: Engelberg, D, et al.
出版: (2008)

Observations of intergranular stress corrosion cracking in a grain-mapped polycrystal.
由: King, A, et al.
出版: (2008)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
由: Rahimi, S, et al.
出版: (2019)

Towards modelling intergranular stress-corrosion cracks using experimentally obtained grain topologies
由: Simonovski, I, et al.
出版: (2010)

Stress assisted intergranular oxidation cracking of Incoloy Alloy 908
由: Morra, M.M.
出版: (2015)

A new method for predicting susceptibility of austenitic stainless steels to intergranular stress corrosion cracking
由: S. Rahimi, et al.
出版: (2020-02-01)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
由: Rahimi, S, et al.
出版: (2009)

In situ observation of intergranular crack nucleation in a grain boundary controlled austenitic stainless steel.
由: Rahimi, S, et al.
出版: (2009)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
由: Babout, L, et al.
出版: (2006)

X-ray microtomographic observation of intergranular stress corrosion cracking in sensitised austenitic stainless steel
由: Babout, L, et al.
出版: (2006)

Cracks in refractory concrete: Transgranular or intergranular?
由: Christian Jung, et al.
出版: (2025-02-01)

Effect of surface machining on intergranular stress corrosion cracking (IGSCC) in sensitised type 304 austenitic stainless steel
由: Rahimi, S, et al.
出版: (2016)

Adaptive 3D algorithm to detect bridging ligaments during intergranular stress corrosion cracking of stainless steel
由: Janaszewski, M, et al.
出版: (2007)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
由: Rahimi, S, et al.
出版: (2012)

Effects of orientation, stress and exposure time on short intergranular stress corrosion crack behaviour in sensitised type 304 austenitic stainless steel
由: Rahimi, S, et al.
出版: (2012)

Calculation of Hydrogen Buildup in the Neighborhood of Intergranular Cracks
由: Zohdi, T.I., et al.
出版: (1998-03-01)

Microstructural characterization of intergranular stress corrosion cracking of 300 series stainless steels in PWR conditions
由: Huang, Y, et al.
出版: (2001)

Experimental validation of intergranular stress corrosion cracking predictive models
由: Saravanan, N
出版: (2022)

Correlations of electrochemical noise, acoustic emission and complementary monitoring techniques during intergranular stress-corrosion cracking of austenitic stainless steel
由: Kovac, J, et al.
出版: (2010)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
由: Stratulat, A, et al.
出版: (2014)

Grain boundary structure and intergranular stress corrosion crack initiation in high temperature water of a thermally sensitised austenitic stainless steel, observed in situ
由: Stratulat, A, et al.
出版: (2014)