High-temperature crack growth in a Ni-base superalloy during sustained load

High-temperature crack growth in a Ni-base superalloy during sustained load

The high-temperature sustained load crack growth behaviour of a Ni-base superalloy was investigated using a combination of mechanical testing in controlled atmosphere, fractographical and microanalytical investigations, and finite element modelling. The results show that the local crack front geomet...

Ausführliche Beschreibung

Bibliographische Detailangaben
Hauptverfasser:	Hornqvist, M, Viskari, L, Moore, K, Stiller, K
Format:	Journal article
Sprache:	English
Veröffentlicht:	Elsevier 2014

Ähnliche Einträge

Intergranular crack tip oxidation in a Ni-base superalloy
von: Viskari, L, et al.
Veröffentlicht: (2013)

Intergranular crack tip oxidation in a Ni-base superalloy
von: Viskari, L, et al.
Veröffentlicht: (2013)

Macro- and micro-mechanical behaviour of a γ′ strengthened Ni-based superalloy at cryogenic temperatures
von: Nitesh Raj Jaladurgam, et al.
Veröffentlicht: (2021-11-01)

Cracking during High-Temperature Deformation of a High-Strength Polycrystalline CoNi-Base Superalloy
von: Daniel Hausmann, et al.
Veröffentlicht: (2022-09-01)

Meta-Dynamic Recrystallization in the Ni-Based Superalloy Haynes 282
von: Emil Eriksson, et al.
Veröffentlicht: (2023-07-01)

High-cycle fatigue behaviour and crack growth mechanism of Ni-base single crystal superalloy under intermediate temperature
von: Quanfeng Xiao, et al.
Veröffentlicht: (2023-07-01)

Predictive Modeling of Arbitrary Loaded TMF Crack Growth in Superalloys
von: Johnson W. Steven, et al.
Veröffentlicht: (2018-01-01)

Simulation of oxidation-nitridation-induced microstructural degradation in a cracked Ni-based superalloy at high temperature
von: Yuan Kang, et al.
Veröffentlicht: (2014-01-01)

Thermomechanical behavior of different Ni-base superalloys during cyclic loading at elevated temperatures
von: Huber Daniel, et al.
Veröffentlicht: (2014-01-01)

The influence of contacting Ni-based single-crystal superalloys on fretting fatigue of Ni-based polycrystalline superalloys at high temperature
von: Fleury, R, et al.
Veröffentlicht: (2014)

Microscopic damage mechanisms during fatigue crack propagation at high temperature in GH4169 superalloy
von: HOU Jie, et al.
Veröffentlicht: (2018-07-01)

High temperature fatigue crack growth in powder processed nickel based superalloy U720Li
von: Tucker, A, et al.
Veröffentlicht: (2002)

Fatigue crack growth from handling surface anomalies in a Nickel based superalloy at high temperature
von: Gourdin Stéphane, et al.
Veröffentlicht: (2014-06-01)

Fatigue crack growth from handling surface anomalies in a nickel based superalloy at high temperature
von: Gourdin Stéphane, et al.
Veröffentlicht: (2014-01-01)

Oxygen changes crack modes of Ni-based single crystal superalloy
von: Xueqiao Li, et al.
Veröffentlicht: (2021-12-01)

Dislocations in a Ni-based superalloy during low temperature creep
von: Rae Catherine, et al.
Veröffentlicht: (2014-01-01)

Influence of orientation and temperature on the fatigue crack growth of directionally solidification superalloys DZ125
von: Shi Yi, et al.
Veröffentlicht: (2018-01-01)

Ultra-high temperature creep of Ni-based SX superalloys at 1250 °C
von: Utada, S, et al.
Veröffentlicht: (2021)

The Analysis of the Residual Stress Evolution during Cycling Oxidation of the Ni-base Superalloys at High Temperature
von: Wojciech J. Nowak*, et al.
Veröffentlicht: (2021-01-01)

Additive manufacturing of Ni-based superalloys: Residual stress, mechanisms of crack formation and strategies for crack inhibition
von: Chuan Guo, et al.
Veröffentlicht: (2023-03-01)

Prevention of hot cracking in Ni-based superalloy via passivation layer formation during additive manufacturing
von: KenHee Ryou, et al.
Veröffentlicht: (2024-11-01)

Grain growth in spray-formed Ni superalloys
von: Underhill, R, et al.
Veröffentlicht: (1995)

Influences of crystal orientations and grain boundary on crack propagation behaviour at room temperature in a polycrystalline Ni-base superalloy
von: Mana HIGAKI, et al.
Veröffentlicht: (2018-03-01)

Effect of crystallographic properties on low cycle fatigue crack initiation at elevated temperature for Ni-based directionally solidified superalloy
von: Takashi YOKOYAMA, et al.
Veröffentlicht: (2016-01-01)

High temperature oxidation behavior of γʹ-strengthened CoNi-base superalloys
von: Yingju Li, et al.
Veröffentlicht: (2024-12-01)

The dynamic recrystallization of the Ni-based superalloy under the supergravity stress and high temperature
von: Wenshuai Wang, et al.
Veröffentlicht: (2024-11-01)

Ultra-High Temperature Creep of Ni-Based SX Superalloys at 1250 °C
von: Satoshi Utada, et al.
Veröffentlicht: (2021-10-01)

In situ diagnostics of damage accumulation in Ni-based superalloys using high-temperature computed tomography
von: Kageyama, K, et al.
Veröffentlicht: (2018)

Dynamic strain aging in Haynes 282 superalloy
von: Hörnqvist Magnus, et al.
Veröffentlicht: (2014-01-01)

Effects of Ni and Cr on the high-temperature oxidation behavior and mechanisms of Co- and CoNi-base superalloys
von: Longjun Li, et al.
Veröffentlicht: (2022-12-01)

The cracking behavior of the new Ni-based superalloy GH4151 in the triple melting process
von: Lei Jia, et al.
Veröffentlicht: (2023-07-01)

Effect of oxygen on creep crack growth in nickel-base superalloys
von: Bain, Kenneth Rees
Veröffentlicht: (2007)

Thermomechanical fatigue crack growth in a cast polycrystalline superalloy
von: Moverare Johan J., et al.
Veröffentlicht: (2014-01-01)

Kinetics of Grain Growth in 718 Ni-Base Superalloy
von: Huda Z., et al.
Veröffentlicht: (2014-10-01)

Phase Transformations in Nickel base Superalloy Inconel 718 during Cyclic Loading at High Temperature
von: Michal Jambor, et al.
Veröffentlicht: (2017-06-01)

Phase Transformations in Nickel base Superalloy Inconel 718 during Cyclic Loading at High Temperature
von: Jambor Michal, et al.
Veröffentlicht: (2017-06-01)

High temperature oxidation of HR120 and 800H Fe-Ni-Cr superalloys /
von: Chong, Pui Ying, 1990-, author, et al.
Veröffentlicht: (2014)

Determination of the high temperature elastic properties and diffraction elastic constants of Ni-base superalloys
von: P.E. Aba-Perea, et al.
Veröffentlicht: (2016-01-01)

Temperature dependence of deformation mechanisms of a new Ni-based superalloy and high-temperature property optimization
von: Pengfei Zhao, et al.
Veröffentlicht: (2023-11-01)

Crack inhibition and crystallographic texture control in an additively manufactured IN738LC Ni-based superalloy
von: Fangxian Zhang, et al.
Veröffentlicht: (2024-11-01)