Evolution of dislocation density distributions in copper during tensile deformation
The evolution of dislocation storage in deformed copper was studied with cross-correlation-based high-resolution electron backscatter diffraction. Maps of 500 μm × 500 μm areas with 0.5 μm step size were collected and analysed for samples deformed in tension to 0%, 6%, 10%, 22.5% and 40% plastic str...