In-Situ monitoring of phase transition and microstructure evolution in ni-based superalloys by electrical resistivity: direct comparison with differential scanning calorimetry and application to case studies
<p>In this study, resistivity measurements are made during continuous heating and cooling on four different Ni-based superalloys of different grain structures and with different phases (i.e., γ′ and carbide). The results are directly compared with differential scanning calorimetry (DSC) profil...
| Main Authors: | , , , |
|---|---|
| Format: | Journal article |
| Language: | English |
| Published: |
Springer
2022
|
| Summary: | <p>In this study, resistivity measurements are made during continuous heating and cooling on four different Ni-based superalloys of different grain structures and with different phases (i.e., γ′ and carbide). The results are directly compared with differential scanning calorimetry (DSC) profiles to identify the material’s resistivity response. The resistivity measurements have been performed using an electro-thermal mechanical testing (ETMT) system having a capability of heating and cooling a sample at a rate of up to 100 K/s by Joule heating, which is not possible with standard heating methods used in previous <em>in-situ</em> microstructure analysis approaches. By comparing different precipitate variations and thermal histories, γ′ volume fraction and precipitate number density are found to be the most important factors determining the resistivity of the materials. <em>In-situ</em> resistivity measurement was applied to several case studies to show that it can provide microstructural information in complex high temperature experiments.</p> |
|---|