CRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESS
High-Tc superconducting YBa2Cu4O8 submicron powders with transition temperature around 80 K were successfully synthesized via citrate gel process at one atmosphere oxygen pressure. An intragrain critical current density of up to 1.3×107A/cm2 at 6 K and H=1 T has been measured by magnetisation method...
| Main Authors: | , , , , |
|---|---|
| Format: | Journal article |
| Language: | English |
| Published: |
1990
|
| _version_ | 1826267957209071616 |
|---|---|
| author | Liu, R Zheng, D Janes, R Campbell, A Edwards, P |
| author_facet | Liu, R Zheng, D Janes, R Campbell, A Edwards, P |
| author_sort | Liu, R |
| collection | OXFORD |
| description | High-Tc superconducting YBa2Cu4O8 submicron powders with transition temperature around 80 K were successfully synthesized via citrate gel process at one atmosphere oxygen pressure. An intragrain critical current density of up to 1.3×107A/cm2 at 6 K and H=1 T has been measured by magnetisation method; this value is comparable to that found in sintered YBa2Cu3O7-δ. The integrain criticalcurrent density, as measured by an a.c. inductive technique, was 103 A/cm2 at 4.2 K; this is in excess of typical values for YBa2Cu3O7-δ. © 1990. |
| first_indexed | 2024-03-06T21:02:13Z |
| format | Journal article |
| id | oxford-uuid:3b416fe9-606f-42a4-b4fc-0356b918bfca |
| institution | University of Oxford |
| language | English |
| last_indexed | 2024-03-06T21:02:13Z |
| publishDate | 1990 |
| record_format | dspace |
| spelling | oxford-uuid:3b416fe9-606f-42a4-b4fc-0356b918bfca2022-03-26T14:06:31ZCRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESSJournal articlehttp://purl.org/coar/resource_type/c_dcae04bcuuid:3b416fe9-606f-42a4-b4fc-0356b918bfcaEnglishSymplectic Elements at Oxford1990Liu, RZheng, DJanes, RCampbell, AEdwards, PHigh-Tc superconducting YBa2Cu4O8 submicron powders with transition temperature around 80 K were successfully synthesized via citrate gel process at one atmosphere oxygen pressure. An intragrain critical current density of up to 1.3×107A/cm2 at 6 K and H=1 T has been measured by magnetisation method; this value is comparable to that found in sintered YBa2Cu3O7-δ. The integrain criticalcurrent density, as measured by an a.c. inductive technique, was 103 A/cm2 at 4.2 K; this is in excess of typical values for YBa2Cu3O7-δ. © 1990. |
| spellingShingle | Liu, R Zheng, D Janes, R Campbell, A Edwards, P CRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESS |
| title | CRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESS |
| title_full | CRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESS |
| title_fullStr | CRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESS |
| title_full_unstemmed | CRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESS |
| title_short | CRITICAL CURRENT DENSITIES OF SUPERCONDUCTING YBA2CU4O8 SYNTHESIZED BY THE CITRATE GEL PROCESS |
| title_sort | critical current densities of superconducting yba2cu4o8 synthesized by the citrate gel process |
| work_keys_str_mv | AT liur criticalcurrentdensitiesofsuperconductingyba2cu4o8synthesizedbythecitrategelprocess AT zhengd criticalcurrentdensitiesofsuperconductingyba2cu4o8synthesizedbythecitrategelprocess AT janesr criticalcurrentdensitiesofsuperconductingyba2cu4o8synthesizedbythecitrategelprocess AT campbella criticalcurrentdensitiesofsuperconductingyba2cu4o8synthesizedbythecitrategelprocess AT edwardsp criticalcurrentdensitiesofsuperconductingyba2cu4o8synthesizedbythecitrategelprocess |