The first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24
A series of new layered uranium(IV) fluorides have been prepared under hydrothermal conditions from UO2, HF, and H3PO4 by using H2N(CH2)nNH2 (n = 3, 4, or 6), and N(CH2-CH2NH2)3 as structure-directing agents. [H3N(CH2)3NH3]U2F 10·2H2O (UFO-1), [H3N(CH2)4-NH3]U2F 10·3H2O (UFO-2), [H3N(CH2)6NH3]U2F 10...
Main Authors: | , , |
---|---|
Format: | Journal article |
Language: | English |
Published: |
1998
|
_version_ | 1797066437221679104 |
---|---|
author | Francis, R Halasyamani, P O'Hare, D |
author_facet | Francis, R Halasyamani, P O'Hare, D |
author_sort | Francis, R |
collection | OXFORD |
description | A series of new layered uranium(IV) fluorides have been prepared under hydrothermal conditions from UO2, HF, and H3PO4 by using H2N(CH2)nNH2 (n = 3, 4, or 6), and N(CH2-CH2NH2)3 as structure-directing agents. [H3N(CH2)3NH3]U2F 10·2H2O (UFO-1), [H3N(CH2)4-NH3]U2F 10·3H2O (UFO-2), [H3N(CH2)6NH3]U2F 10·2H2O (UFO-3), and [HN(CH2CH2NH3)3]-U5F 24 (UFO-4) have been characterized by single-crystal X-ray diffraction, thermogravimetric analysis, BET isotherms, and magnetic susceptibility measurements. UFO-1, 2, 3, and 4 contain negatively charged uranium fluoride (UF) layers constructed from linked UFn polyhedra separated by charge balancing organic cations and occluded water molecules. In UFO-1, 2, and 3, the layers are constructed from equivalent UF9 tricapped trigonal prisms that share three edges and two corners, whereas UFO-4 contains both UF8 bicapped trigonal prisms and UF9 tricapped trigonal prisms. We have demonstrated that the interlamellar organic cations in these materials can be ion-exchanged with a large variety of alkali, alkaline earth, and transition metal cations, thus providing a low-temperature route to new condensed mixed metal uranium fluorides. The magnetic susceptibility data indicate that UFO-1, 2, and 3 exhibit Curie-Wiess behavior between room temperature and 20 K. [Crystal data: UFO-1, monoclinic, space group P21/c (no. 14), a = 10.715(1) Å, b = 7.097(1) Å, c = 8.767(1) Å, β = 93.804(6)°, V = 665.21(1) Å3 (T = 150 K), Z = 2, R(F) = 5.42%, Rw(F) = 6.79%; UFO-2, triclinic, space group P1 (no. 2), a = 12.024(2) Å, b = 7.149(3) Å, c = 8.765(2) Å, α = 90.063(4)°, β = 107.133(5)°, γ = 92.098(3)°, V = 719.49(3) Å3 (T = 150 K), Z = 2, R(F) = 8.05%, Rw(F) = 10.11%; UFO-3, monoclinic, space group P21/c (no. 14), a = 13.800(2) Å, b = 7.056(1) Å, c = 8.720(1) Å, β = 108.338(6)°, V = 805.97(2) Å3 (T = 150 K), Z = 2, R(F) = 3.64%, Rw(F) = 4.65%; UFO-4, triclinic, space group P1 (no. 2), a = 11.534(2) Å, b = 11.532-(4) Å, c = 9.634(2) Å, α = 104.034(4)°, β = 101.112(8)°, γ = 93.922(4)°, V = 1210.9(5) Å3 (T = 150 K), Z = 2, R(F) = 6.12%, Rw(F) = 8.19%.]. |
first_indexed | 2024-03-06T21:42:03Z |
format | Journal article |
id | oxford-uuid:4842ed53-4513-4bf2-a7d2-1621146f017f |
institution | University of Oxford |
language | English |
last_indexed | 2024-03-06T21:42:03Z |
publishDate | 1998 |
record_format | dspace |
spelling | oxford-uuid:4842ed53-4513-4bf2-a7d2-1621146f017f2022-03-26T15:24:43ZThe first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24Journal articlehttp://purl.org/coar/resource_type/c_dcae04bcuuid:4842ed53-4513-4bf2-a7d2-1621146f017fEnglishSymplectic Elements at Oxford1998Francis, RHalasyamani, PO'Hare, DA series of new layered uranium(IV) fluorides have been prepared under hydrothermal conditions from UO2, HF, and H3PO4 by using H2N(CH2)nNH2 (n = 3, 4, or 6), and N(CH2-CH2NH2)3 as structure-directing agents. [H3N(CH2)3NH3]U2F 10·2H2O (UFO-1), [H3N(CH2)4-NH3]U2F 10·3H2O (UFO-2), [H3N(CH2)6NH3]U2F 10·2H2O (UFO-3), and [HN(CH2CH2NH3)3]-U5F 24 (UFO-4) have been characterized by single-crystal X-ray diffraction, thermogravimetric analysis, BET isotherms, and magnetic susceptibility measurements. UFO-1, 2, 3, and 4 contain negatively charged uranium fluoride (UF) layers constructed from linked UFn polyhedra separated by charge balancing organic cations and occluded water molecules. In UFO-1, 2, and 3, the layers are constructed from equivalent UF9 tricapped trigonal prisms that share three edges and two corners, whereas UFO-4 contains both UF8 bicapped trigonal prisms and UF9 tricapped trigonal prisms. We have demonstrated that the interlamellar organic cations in these materials can be ion-exchanged with a large variety of alkali, alkaline earth, and transition metal cations, thus providing a low-temperature route to new condensed mixed metal uranium fluorides. The magnetic susceptibility data indicate that UFO-1, 2, and 3 exhibit Curie-Wiess behavior between room temperature and 20 K. [Crystal data: UFO-1, monoclinic, space group P21/c (no. 14), a = 10.715(1) Å, b = 7.097(1) Å, c = 8.767(1) Å, β = 93.804(6)°, V = 665.21(1) Å3 (T = 150 K), Z = 2, R(F) = 5.42%, Rw(F) = 6.79%; UFO-2, triclinic, space group P1 (no. 2), a = 12.024(2) Å, b = 7.149(3) Å, c = 8.765(2) Å, α = 90.063(4)°, β = 107.133(5)°, γ = 92.098(3)°, V = 719.49(3) Å3 (T = 150 K), Z = 2, R(F) = 8.05%, Rw(F) = 10.11%; UFO-3, monoclinic, space group P21/c (no. 14), a = 13.800(2) Å, b = 7.056(1) Å, c = 8.720(1) Å, β = 108.338(6)°, V = 805.97(2) Å3 (T = 150 K), Z = 2, R(F) = 3.64%, Rw(F) = 4.65%; UFO-4, triclinic, space group P1 (no. 2), a = 11.534(2) Å, b = 11.532-(4) Å, c = 9.634(2) Å, α = 104.034(4)°, β = 101.112(8)°, γ = 93.922(4)°, V = 1210.9(5) Å3 (T = 150 K), Z = 2, R(F) = 6.12%, Rw(F) = 8.19%.]. |
spellingShingle | Francis, R Halasyamani, P O'Hare, D The first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24 |
title | The first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24 |
title_full | The first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24 |
title_fullStr | The first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24 |
title_full_unstemmed | The first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24 |
title_short | The first fully fluorinated organically templated materials: Synthesis, structures, and physical properties of [H3N(CH2)(3)NH3]U2F10 center dot 2H(2)O, [H3N(CH2)(4)NH3]U2F10 center dot 3H(2)O, [H3N(CH2)(6)NH3]U2F10 center dot 2H(2)O, and [HN(CH2CH2NH3)(3)]U5F24 |
title_sort | first fully fluorinated organically templated materials synthesis structures and physical properties of h3n ch2 3 nh3 u2f10 center dot 2h 2 o h3n ch2 4 nh3 u2f10 center dot 3h 2 o h3n ch2 6 nh3 u2f10 center dot 2h 2 o and hn ch2ch2nh3 3 u5f24 |
work_keys_str_mv | AT francisr thefirstfullyfluorinatedorganicallytemplatedmaterialssynthesisstructuresandphysicalpropertiesofh3nch23nh3u2f10centerdot2h2oh3nch24nh3u2f10centerdot3h2oh3nch26nh3u2f10centerdot2h2oandhnch2ch2nh33u5f24 AT halasyamanip thefirstfullyfluorinatedorganicallytemplatedmaterialssynthesisstructuresandphysicalpropertiesofh3nch23nh3u2f10centerdot2h2oh3nch24nh3u2f10centerdot3h2oh3nch26nh3u2f10centerdot2h2oandhnch2ch2nh33u5f24 AT ohared thefirstfullyfluorinatedorganicallytemplatedmaterialssynthesisstructuresandphysicalpropertiesofh3nch23nh3u2f10centerdot2h2oh3nch24nh3u2f10centerdot3h2oh3nch26nh3u2f10centerdot2h2oandhnch2ch2nh33u5f24 AT francisr firstfullyfluorinatedorganicallytemplatedmaterialssynthesisstructuresandphysicalpropertiesofh3nch23nh3u2f10centerdot2h2oh3nch24nh3u2f10centerdot3h2oh3nch26nh3u2f10centerdot2h2oandhnch2ch2nh33u5f24 AT halasyamanip firstfullyfluorinatedorganicallytemplatedmaterialssynthesisstructuresandphysicalpropertiesofh3nch23nh3u2f10centerdot2h2oh3nch24nh3u2f10centerdot3h2oh3nch26nh3u2f10centerdot2h2oandhnch2ch2nh33u5f24 AT ohared firstfullyfluorinatedorganicallytemplatedmaterialssynthesisstructuresandphysicalpropertiesofh3nch23nh3u2f10centerdot2h2oh3nch24nh3u2f10centerdot3h2oh3nch26nh3u2f10centerdot2h2oandhnch2ch2nh33u5f24 |