Crack deflection and interfacial fracture energies in alumina/SiC and alumina/TiN nanocomposites
Crack/particle interactions in Al2O3/SiC and Al2O3/TiN nanocomposites have been observed by TEM on samples containing cracks produced by Vickers indentations. No significant crack deflection by intragranular SiC particles or microcracking around nanoparticles was found. Intergranular cracks were obs...
Hlavní autoři: | Jiao, S, Jenkins, M |
---|---|
Médium: | Conference item |
Vydáno: |
1997
|
Podobné jednotky
-
Interfacial fracture energy-mechanical behaviour relationship in Al2O3/SiC and Al2O3/TiN nanocomposites
Autor: Jiao, S, a další
Vydáno: (1997) -
Erosive wear of alumina/SiC nanocomposite ceramics
Autor: Lawrence, C, a další
Vydáno: (1999) -
Subsurface damage analysis by TEM and 3D FIB crack mapping in alumina and alumina/5vol.%SiC nanocomposites
Autor: Wu, H, a další
Vydáno: (2003) -
Wet erosion behaviour of low SiC alumina-SiC nanocomposites
Autor: Kara, H, a další
Vydáno: (2002) -
Indentation fracture toughness and surface flaw analysis of sintered alumina/SiC nanocomposites
Autor: Anya, C, a další
Vydáno: (1996)